Disertación de Maestría
DOI
10.11606/D.58.2011.tde-15122011-094523
Documento
Autor
Nombre completo
Carla Cecília Alandia Román
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2011
Director
Tribunal
Panzeri, Heitor (Presidente)
Souza, Evelise Machado de
Tirapelli, Camila
Título en portugués
Análise da estabilidade de cor e rugosidade de superfície de compósitos submetidos à fumaça de cigarro
Palabras clave en portugués
alteração de cor
fumaça de cigarro
resina composta
rugosidade de superfície
Resumen en portugués
O objetivo deste estudo foi avaliar a estabilidade de cor e rugosidade de superfície de 3 compósitos odontológicos com partículas diferentes: nanohíbrido (Tetric N-Ceram - Ivoclar Vivadent), híbrido (Z250 - 3M ESPE) e microhíbrido com matriz silorano (Filtek P90 3M - ESPE), submetidos à fumaça de cigarro. Para isso, foram obtidos 60 corpos-de-prova (8mm de diâmetro X 2mm de espessura), 20 para cada tipo de material restaurador utilizado, dos quais 10 receberam polimento com lixas dágua em abrasividades decrescentes (Grupo1) e a outra metade não foi submetida a nenhum tipo de acabamento/polimento ficando sob efeito apenas de uma matriz de poliéster (Grupo 2). Após armazenamento dos corpos de prova em água destilada a 37°C por 24 horas, foram realizadas as primeiras leituras de cor (Colorímetro Vita Easy Shade) na escala de cor CIEL*a*b* e rugosidade superficial (Rugosímetro Surfcorder SE 1700 - Kosakalab). Em seguida, as amostras foram expostas à fumaça de 20 cigarros por um período de 10 minutos cada, (Marlboro - Philip Morris), sendo que entre um cigarro e outro as amostras foram submetidas à escovação em dispositivo padronizado e lavagem em água corrente. Após ação do número total de cigarros, foram realizadas leituras finais de cor e rugosidade. Os valores de ΔE, ΔL, Δa e Δb foram analisados estatisticamente utilizando 2 way ANOVA e Teste de Bonferroni (p<0.05) e os valores de rugosidade média (Ra) foram analisados isoladamente para cada tipo de material (teste t Student, p < 0.05). Verificou-se que o compósito Tetric N apresentou maior alteração de cor, em níveis clinicamente inaceitáveis (ΔE>3,3) e de rugosidade de superfície em relação aos demais compósitos quando utilizada a tira de poliéster como acabamento. Concluiu-se que a ausência de polimento aumenta a capacidade manchadora do cigarro sobre todos os compósitos e a rugosidade de superfície dos materiais, com exceção de P90.
Título en inglés
Color stability and surface roughness of dental composites exposed to cigarette smoke
Palabras clave en inglés
cigarette smoke
color stability
composite resin
surface roughness
Resumen en inglés
The purpose of this study was to evaluate the color stability and surface roughness of three dental composites with different type of fillers: Nanohybrid (Tetric N-Ceram), Hybrid (Filtek Z250-3M ESPE) and Microhybrid silorane based composite (Filtek P90- 3M ESPE), exposed to cigarette smoke. 20 specimens (8mm diameter X 2mm thickness) of each material were prepared and separated into two groups (n=10) according to the surface treatment : Group 1- polymerization through a polyester film strip and polishing with water sandpaper in decreasing abrasiveness (600, 800 e 1200); and Group 2- polymerization through a polyester film strip, without any polishing. After immersion in destilled water 37° for 24 hours, baseline color of all specimens was measured using reflectance spectrophotometer (Easy Shade - Vita) with CIEL*a*b* system, surface roughness was also measured using a rugosimeter (SJ-201P Mitutoyo, Tokyo, Japan). After base line measurements, the specimens were exposed to smoke from 20 cigarettes in 10 minutes each, (Marlboro - Philip Morris), between one cigarette and other, the specimens were submitted to brushing in a standardized device and washed with water. After the action of the total number of cigarettes, final measurements of color and surface roughness were performed. Values of ΔE, ΔL, Δa e Δb were statistically analyzed using 2 way ANOVA e Teste de Bonferroni (p<0.05) and values of average surface roughness (Ra) were analyzed separately for each type of material (teste t Student, p < 0.05). It was found that the composite Tetric N-Ceram showed increased of surface roughness and greater color change in clinically unacceptable levels (ΔE>3,3), in comparison with the other composites when used the polyester strip without polishing. It was concluded that the absence of polishing increases the cigarette staining and surface roughness on all composites except for Filtek P90.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-09-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.