Thèse de Doctorat
DOI
10.11606/T.58.2017.tde-17022016-170119
Document
Auteur
Nom complet
Denise Pupim
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2015
Directeur
Jury
Mattos, Maria da Gloria Chiarello de (Président)
Brandini, Daniela Atili
Orsi, Iara Augusta
Souza, Valéria Oliveira Pagnano de
Vaz, Luís Geraldo
Titre en portugais
Avaliação da alteração de rugosidade de superfície e dispersão de íons de ligas metálicas odontológicas submetidas a ensaio de tribocorrosão experimental
Mots-clés en portugais
Fundição
Íons metálicos
Ligas metálicas
Rugosidade
Tribocorrosão
Resumé en portugais
Este estudo teve como objetivo avaliar a alteração da rugosidade superficial e a dispersão de íons para o meio após tribocorrosão experimental das ligas CoCrMo, NiCr e NiCrTi, comercialmente utilizadas na fabricação de próteses odontológicas, utilizando solução de saliva artificial (Fusayama) como eletrólito com valores de pH 3,0; 6,5 e 9,0. Foram fundidas 15 amostras de cada liga (Ø13x2mm) por chama e 15 por máquina de fundição com atmosfera inerte de argônio, sendo cinco amostras para cada pH analisado. A tribocorrosão experimental foi realizada na configuração esfera sobre superfície, utilizando esfera de zircônia (Ø10mm), em equipamento de ciclagem vertical, simulando o movimento do ciclo mastigatório, com aplicação de 5N de carga e monitoramento do potencial de circuito aberto (OCP). O sistema operou a velocidade de 60 ciclos por minuto, totalizando 7500 ciclos após 15 minutos de ensaio, equivalente ao tempo de contato dental diário. Foi utilizada saliva artificial de pH 3,0; 6,5 e 9,0 e leituras de rugosidade de superfície foram realizadas antes e após os ensaios de tribocorrosão experimental em microscópio confocal a laser. A saliva utilizada foi armazenada em tubos de Falcon DNA-free e submetida à quantificação da dispersão de íons metálicos para a solução, por meio de análise de ICP-MS. O comportamento das ligas em contato com a esfera de zircônia durante o ensaio de tribocorrosão experimental realizado em potencial de circuito aberto foi alterado em função do pH do meio (P<0,001) e da técnica de fundição utilizada (P<0,001). Todas as amostras apresentaram tendência à repassivação após a remoção do contato com a esfera, indicando formação de novo filme protetor na superfície da liga. A liberação de íons foi maior nas amostras fundidas por chama e em contato com pH 3,0 (ácido), sendo o analito níquel liberado em maior concentração (P=0,010). Entretanto, os valores encontrados estão abaixo dos limites indicados como causadores de citotoxicidade e alterações celulares. Os resultados indicam que as amostras fundidas por chama apresentaram rugosidade de superfície estatisticamente maior que as fundidas por plasma (P=0,042), sendo observado nessas amostras a presença de defeitos na superfície e possíveis falhas de fundição que favorecem o processo corrosivo. O pH da saliva e a técnica de fundição exerceram influência sobre o comportamento de repassivação das ligas, rugosidade de superfície e quantidade de íons liberada para o meio, sendo os melhores resultados encontrados quando a técnica de fundição por plasma foi utilizada.
Titre en anglais
Evaluation of changes in surface roughness and ion release from dental casting alloys after an experimental tribocorrosion process
Mots-clés en anglais
Casting
Metal alloys
Metallic ions
Roughnes
Tribocorrosion
Resumé en anglais
The aim of this study was to evaluate the changes in surface roughness and ions release to the environment after experimental tribocorrosion of CoCrMo, NiCr and NiCrTi alloys, commercially applied in dental prosthesis, using artificial saliva solution (Fusayama) as electrolyte with different levels of pH (3.0; 6.5 and 9.0). Fifteen samples were casted by flame from each alloy (Ø13x2mm) and 15 by plasma in a casting machine with an inert atmosphere (argon), five samples for each pH analyzed. The experimental tribocorrosion was performed in a ball-on-flat configuration, using a zirconia ball (Ø10mm) in vertical cycling equipment, simulating the masticatory cycle movement, applying 5N of load and recording the open circuit potential (OCP). The system operated at 60 cycles per minute, a total of 7500 cycles after 15 minutes, corresponding to the daily tooth contact. Artificial saliva at pH 3.0; 6.5 and 9.0 was used and surface roughness measurements were performed before and after the experimental tribocorrosion tests in a laser confocal microscope. After the tests, the saliva was stored in a DNA-free Falcon tubes and subjected to measurement of the ion release to the solution by means of ICP-MS analysis. The behavior of the alloys in contact with the zirconia ball during the experimental tribocorrosion performed in open circuit potential changed according to the pH (P<0.001) and the casting technique (P<0.001). All samples trended to repassivate when the ball contact was removed, indicating new formation of the protective film on alloy surface. The ion release was higher in the samples casted by flame and in contact with pH 3.0 (acid), nickel analyte being released in a higher concentration (P=0.010). However, the values found are below the limits specified to induce cytotoxicity and cellular changes. The results reflected that the samples casted by flame presented surface roughness statistically greater than those casted by plasma (P=0.042) and it was observed in these samples the presence of surface defects and possible casting flaws that enhance the corrosion process. The pH of the saliva and the casting technique presented influence on the repassivation behavior of the alloys, surface roughness and quantity of ions released into the environment, where the best results were found when the plasma casting technique was used.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-08-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.