Tesis Doctoral
DOI
10.11606/T.58.2009.tde-26032010-144643
Documento
Autor
Nombre completo
Hilmo Barreto Leite Falcão Filho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2009
Director
Tribunal
Antunes, Rossana Pereira de Almeida (Presidente)
Ferracioli, Renata Cristina Silveira Rodrigues
Margonar, Rogério
Pinelli, Ligia Antunes Pereira
Souza, Raphael Freitas de
Título en portugués
Análise da força de retenção de cimentos resinosos em modelo representativo da técnica de cimentação passiva para implantes osseointegráveis
Palabras clave en portugués
Materiais Dentários
Prótese Dentária Fixada por Implante
Retenção em Prótese Dentária
Resumen en portugués
O objetivo deste estudo foi analisar a força de retenção de dois cimentos resinosos utilizados na técnica de cimentação passiva para implantes osseointegráveis, Panavia F e RelyX U100, avaliando essa propriedade na sua aplicação em espécimes de três tipos de diferentes metais, NiCr (Verabond 2, Aalba Dental), NiCrTi (Tilite Ômega, Talladium) e Titânio (Ti c.p., grau 2, Realum), submetidos ou não à termociclagem. Noventa e seis cilindros calcináveis (Conexão Sistemas de Próteses) foram encerados de forma padronizada, fundidos (32 cilindros em cada tipo de liga) e cimentados sobre cilindros de titânio (Conexão Sistemas de Próteses). Os corpos-de-prova foram distribuídos em 12 grupos (n = 8) de acordo com o tipo de liga, cimento e ciclagem térmica. Todos os espécimes foram submetidos a imersão em água destilada a 37º C por 24 horas, entretanto apenas metade deles a um ensaio de termociclagem em uma máquina de simulação de ciclos térmicos MSCT-3 por 5000 ciclos durante 30 dias. Todos os corpos-de-prova foram submetidos a ensaios de tração em uma máquina de ensaios mecânicos EMIC-DL2000 (velocidade = 5mm / min e célula de carga = 500 Kgf ). A análise estatística evidenciou resistência de união à tração do cimento RelyX U100 superior ao cimento Panavia F, independente do tipo de metal utilizado, com médias de até 71,18 Kgf e 55,08 Kgf respectivamente. O ensaio de termociclagem não exibiu interferência na resistência de união de ambos cimentos.
Título en inglés
Analysis of resin cement retention strength in a representative model of passive cementation technique for osseointegration implants
Palabras clave en inglés
Dental Materials
Dental Prosthesis
Dental Prosthesis Retention
Implant-Supported
Resumen en inglés
The aim of this study was to analyze the bond strength of two resin cements used in the passive cementation technique for osseointegrated implants, Panavia F and RelyX U100, evaluating this property on its application in specimens of three different metal types, NiCr (Verabond 2, Dental Aalba), NiCrTi (Tilite Omega, Talladium) and Titanium (Ti c.p., degree 2, Realum), submitted or not to termocycling assay. Ninety six calcined cylinders (Conexão Sistemas de Próteses) had been waxed of standardized form, casted (32 in each type of league) and cemented on titanium cylinders (Conexão Sistemas de Próteses). The specimens were distributed enter 12 groups (n = 8) in accordance with the type of metal, cement and thermocycling. All specimens were submitted to an immersion in distilled water at 37ºC for 24 hours, however only half of them to a termocycling assay in a simulation thermal cycles machine MSCT-3 for 5000 cycles during 30 days. All specimens were submitted to a tensile test in a mechanical test machine EMIC-DL2000 (speed = 5mm/min and cell load = 500Kgf). The statistics analysis evidenced tensile strength of the RelyX U100 cement greater than Panavia F cement independent of the metal league type used with averages until 71,18 Kgf and 55,08 Kgf respectively. The termocycling assay did not show interference in the tensile strength of both cements.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
do_Hilmo_Falcao.pdf (2.14 Mbytes)
Fecha de Publicación
2010-10-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.