Thèse de Doctorat
DOI
10.11606/T.58.2011.tde-21092011-142811
Document
Auteur
Nom complet
Carolina Paes Torres Mantovani
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2011
Directeur
Jury
Borsatto, Maria Cristina (Président)
Myaki, Silvio Issáo
Pardini, Luiz Carlos
Serrano, Kranya Victoria Diaz
Telles, Paloma Dias da Silva
Titre en portugais
Análise das propriedades físicas e químicas da dentina de dentes decíduos e permanentes - estudo in vitro
Mots-clés en portugais
Dente decíduo
Dente permanente
Dentina
Propriedades físicas
Propriedades químicas
Resumé en portugais
A exata composição e a micromorfologia da dentina de dentes decíduos ainda são pouco estudadas e conhecidas, e a literatura existente apresenta achados controversos. Os resultados de pesquisas realizadas em dentes permanentes são frequentemente extrapolados para dentes decíduos, sendo que a maioria dos trabalhos explora estes substratos de maneira isolada. É necessário, portanto, conhecer a composição e a estrutura da dentina de dentes decíduos e determinar em quais aspectos este tecido realmente difere da dentina de dentes permanentes. A comparação dos dois substratos é fundamental para que sejam estabelecidos protocolos preventivos e restauradores, bem como no desenvolvimento de materiais e técnicas específicos e efetivos para dentes decíduos e permanentes. Assim, o objetivo do presente estudo foi realizar uma análise comparativa in vitro da dentina de dentes decíduos e permanentes, avaliando suas propriedades físicas e químicas. As propriedades físicas analisadas foram a Permeabilidade (n = 15), a Microdureza (n = 10), a Radiodensidade (n = 10) e a Resistência Coesiva (Ultimate Tensile Strength) (n = 15). As propriedades químicas foram o mapeamento de superfície dentinária por Microfluorescência de Raios-X por Energia Dispersiva (μFRX) (n = 10) e Espectroscopia Raman por Transformada de Fourier (FT-Raman) (n = 10). Os dados foram analisados quanto a sua distribuição e homogeneidade. Na análise de Microdureza, a distribuição dos dados não foi normal e empregou-se o teste não paramétrico de Mann-Whitney para a análise estatística. Para os demais testes, a distribuição dos dados apresentou-se normal e homogênea. Assim, para a análise de Permeabilidade e Radiodensidade foi utilizada Análise de Variância a um critério: tipo de substrato (p<0,05); para o teste de Microtração, empregou-se Análise de Variância a dois critérios (p<0,05): tipo de substrato e profundidade; os dados de Microfluorescência de Raios-X por Energia Dispersiva e Espectroscopia Raman por Transformada de Fourier foram analisados pelo teste t de Student. Considerando-se as limitações de um estudo in vitro, os achados demonstraram que em relação às propriedades físicas, a dentina de dentes decíduos apresentou maior permeabilidade, menor radiodensidade e menor resistência coesiva quando comparada à dentina de dentes permanentes. Entretanto, a microdureza foi semelhante para os dois tecidos dentinários. Para as propriedades químicas avaliadas, constatou-se que a dentina de dentes decíduos apresentou menor conteúdo em peso de Cálcio (%) e da proporção Ca/P (%) e maior porcentagem em conteúdo de Carbonato. No entanto, a quantidade de Fósforo, Fosfato e o conteúdo orgânico, não diferiram dos resultados obtidos na dentina de dentes permanentes.
Titre en anglais
Analysis of the physical and chemical properties of the dentin of primary and permanent teeth - an in vitro study
Mots-clés en anglais
chemical properties
dentin
physical properties
tooth deciduous
tooth permanent
Resumé en anglais
There is still little research and information on the precise composition and the micromorphology of the dentin of primary teeth, and the existing literature reveals controversial findings. The results of studies in permanent teeth are frequently extrapolated to primary teeth, and the majority of works explores these substrates alone. It is thus necessary to know the composition and structure of the dentin of primary teeth and determine in which ways this tissue actually differs from the dentin of permanent teeth. Comparison of these substrates under different aspects is fundamental to establish preventive and restorative protocols, as well as materials and techniques that are specific and effective for primary and permanent teeth. Therefore, the aim of the present in vitro study was to perform a comparative analysis of the dentin of primary and permanent teeth by evaluating its physical and chemical properties. For the physical analysis, Permeability (n = 15), Microhardness (n = 10), Radiodensity (n = 10) and Ultimate Tensile Strength (n = 15) tests were performed. Chemical analysis comprised dentin surface mapping by Energy Dispersive X-ray Microfluorescence (μFRX) (n = 10) and Fourier transform (FT) Raman spectroscopy (n = 10). Data distribution and homogeneity were analyzed. In the Microhardness test, data distribution was not normal and the Mann-Whitney non-parametric test was used for statistical analysis. For the other tests, data distribution was normal and homogenous. Thus, one-way analysis of variance (type of substrate) was used for the Permeability and Radiodensity tests (p<0.05); two-way analysis of variance (type of substrate and depth) was used for the Microtensile Bond Strength test (p<0.05); data from Energy Dispersive X-ray Microfluorescence (μFRX) (n = 10) and Fourier transform (FT) Raman spectroscopy were analyzed using the Students t-test. Considering the limitations of an in vitro investigation, the findings revealed that with respect to the physical properties, the dentin of primary teeth presented greater permeability, lower radiodensity and lower ultimate bond strength of substrate when compared with the dentin of permanent teeth. Nevertheless, the microhardness was similar for both dentin tissues. Regarding the chemical properties, the dentin of primary teeth presented a smaller amount of Calcium and Ca/P (wt%) and, greater amount of Carbonate. However, the amount of Phosphorus and Phosphate and the organic content, did not differ from the results obtained in the dentin of permanent teeth.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-04-19
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.