Mémoire de Maîtrise
DOI
10.11606/D.58.2010.tde-13082010-081953
Document
Auteur
Nom complet
Marcelo Rodrigues Azenha
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2010
Directeur
Jury
Barros, Valdemar Mallet da Rocha (Président)
Ferreira, Paulo Martins
Peitl Filho, Oscar
Titre en portugais
Resposta óssea ao Biosilicato® e ao Biosilicato®Vítreo implantados em fêmur de coelhos
Mots-clés en portugais
Biocompatibilidade
Bioglass 45S5
Biosilicato
Resposta Óssea
Resumé en portugais
O objetivo do presente estudo foi avaliar histologicamente e histomorfometricamente a resposta óssea a três composições de Biosilicato com diferentes fases de cristalização (Vítreo, 1F e 2F) comparando-as com o Bioglass®45S5, que foi empregado como controle. Cilindros de Biosilicato 2F, Biosilicato 1F, Biosilicato®vítreo e Bioglass®45S5 foram implantados em fêmur de coelhos e as amostras obtidas após 8 e 12 semanas da colocação, sendo as mesmas preparadas para análise histológica e histomorfométrica utilizando microscopia de luz. Nesses períodos foi avaliada a resposta óssea e o contato direto osso/implante na porção cortical e no canal medular do fêmur de todos os materiais. A maior quantidade de contato osso implante na região cortical, após 8 semanas, foi observada no material Biosilicato 2F, seguido pelo Biosilicato 1F, Bioglass®45S5 e Biosilicato®vítreo. A análise estatística não evidenciou diferença estatisticamente significante entre os materiais Biosilicato 1F e 2F (p=0,06). Entretanto, nesse período, esses materiais mostraram diferenças estatisticamente significantes em relação aos materiais Biosilicato®vítreo e Bioglass®45S5 (p=0,02). Após 12 semanas o Biosilicato 2F também apresentou os melhores resultados, seguido pelo Bioglass®45S5, Biosilicato®vítreo e Biosilicato 1F, sem contudo serem observadas diferenças estatisticamente significantes (p>0,05). Avaliando a porção medular no período de 8 semanas, observa-se maior formação óssea ao redor do implante de Biosilicato®vítreo, seguido pelos implantes de Bioglass®45S5, Biosilicato 2F e Biosilicato 1F. Decorridas 12 semanas, observa-se melhor resposta óssea nos implantes de Biosilicato 1F, seguido pelos implantes de Biosilicato 2F, Biosilicato®vítreo e Bioglass®45S5, sem contudo serem observadas diferenças estatisticamente significantes entre os materiais ou tempos analisados. Os resultados do presente trabalho demonstram o excelente comportamente biológico das cerâmicas de Biosilicato®.
Titre en anglais
Bone response to Biosilicate® and Biosilicate®Vítreo implanted in rabbit femur
Mots-clés en anglais
Biocompatibility
Bioglass 45S5
Biosilicate
Bone response
Resumé en anglais
The aim of this study was to investigate the histological and histomorphometric bone responses to three Biosilicate® with different crystal phases (Vítreo, 1F and 2F) compared to Bioglass®45S5 used as control. Rods of Biosilicate 2F, Biosilicate 1F, Biosilicate®vítreo, and Bioglass45S5 were implanted in rabbits femurs. Implants were harvested at 8 and 12 weeks and prepared for histological and histomorphometric analyses at light microscope level. At these periods bone response and bone-to-implant contact were evaluated at cortical and medullar portion. Considering bone-to-Implant contact at cortical portion Biosilicate 2F presented the highest bone formation, followed by Biosilicate 1F, Bioglass®45S5, and Biosilicate®vítreo (eight weeks). Biosiliacate 1F and 2F presented similar results with no statistic difference (p=0,06). However, in this period Biosilicate 2F demonstrated higher values than Bioglass®45S5 and Biosilicato®vítreo (p=0,02). After twelve weeks direct bone contact was similar between all tested materials (Biosilicate 2F > Bioglass®45S5 > Biosilicate®vítreo > Biosilicate 1F) with no statistically significant difference (p>0,05). When medullar portion was evaluated Biosilicate®vítreo presented a higher amount of new formed bone followed by Bioglass®45S5, Biosilicate 2F, and Biosilicate 1F (eight weeks). After twelve weeks Biosilicate 1F demonstrated the best result, followed by Biosilicate 2F, Biosilicate®vítreo, and Bioglass®45S5. No statistically significant difference between the materials or the periods was observed (p>0,05).All the Biosilicate® glassceramics appeared to have an excellent behavior at biological environment.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
me_marcelo_azenha.pdf (1.15 Mbytes)
Date de Publication
2010-10-01
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.