Mémoire de Maîtrise
DOI
10.11606/D.59.2011.tde-12092012-173435
Document
Auteur
Nom complet
Nadia Guerra Macedo
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2011
Directeur
Jury
Rosolen, Jose Mauricio (Président)
Blácido, Delia Rita Tapia
Montoro, Luciano Andrey
Titre en portugais
Estudo e desenvolvimento de grafite como agente anti-chama para PVC
Mots-clés en portugais
anti-chama
grafite
óxido de grafite
PVC
Resumé en portugais
O PVC é um dos principais polímeros termoplásticos da atualidade graças à sua grande versatilidade. Entretanto, uma de suas características é a baixa estabilidade térmica, sendo necessário o emprego de aditivos em sua estrutura. Uma das maiores preocupações mundiais é a segurança, sendo que muitos produtos levam proteção anti-chama em sua composição. Entre os vários agentes retardadores de chama a grafite aparece como um material promissor e pouco estudado. No presente trabalho foi estudada uma série de grafites com propriedades anti-chama oriundas de óxido de grafite "flake". O óxido de grafite foi submetido a vários tratamentos térmicos em atmosfera para a obtenção de grafites expandidas. O comportamento anti-chama dessas grafites foi testado adicionando-se 20% em peso no PVC. Membranas desses compósitos foram preparadas utilizando-se um "doctor blade". Os compósitos de grafites produzidas foram caracterizados por microscopia de varredura eletrônica e análise térmica. Isotermas de adsorção/dessorção de N2 também foram coletadas para determinação de área superficial específica e distribuição de poros. A grafite com melhores propriedades anti-chama foi aquela obtida em temperatura mais elevada, 900oC, ou seja, a grafite com mais elevada área superficial específica e com maior capacidade de produção de fuligem.
Titre en anglais
Study and development of graphite as fire retardant agent for PVC.
Mots-clés en anglais
fire retardant
graphite
graphite oxide
PVC
Resumé en anglais
PVC is one of the most important thermoplastic polymers because of its versatility. However, like other polymers, for many technological uses, there is a need to enhance its thermal stability. Security is a global concern, so, the use of some fire retardants is required in polymer composites. Expanded graphite appears as a cleaner type of fire retardants, not well known yet. In the present work, expanded graphite obtained from the graphite oxide was studied. It were prepared PVC composite-membranes with 20 weight % of expanded graphite employing Doctor Blade. The samples were characterized by scanning electron microscope, thermogravimetric analysis and N2 adsorption/desorption isotherms were also collected for the determination of specific surface area and porous distribuition. The results show that the best fire retardant behaviour was achieved by the expanded graphite at 900oC, the graphite with the higher specific surface area and with the largest capacity of soot production.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
dissrtNadiaGMacedo.pdf (20.27 Mbytes)
Date de Publication
2012-09-21
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.