Disertación de Maestría
DOI
10.11606/D.74.2014.tde-06052014-085046
Documento
Autor
Nombre completo
Jaiber Humberto Rodriguez Llanos
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2014
Director
Tribunal
Vercik, Andrés (Presidente)
Beppu, Marisa Masumi
Rigo, Eliana Cristina da Silva
Título en portugués
Propriedades físicas de filmes de quitosana dopados como condutores iônicos
Palabras clave en portugués
Biossensor
Eletrônica verde
Filmes
Intumescimento
Propriedades mecânicas
Quitosana
Transporte
Resumen en portugués
O desenvolvimento de novos materiais a partir de elementos biodegradáveis com durabilidade considerável, versatilidade apreciável e baixo custo tem grande interesse na aplicação da bio-eletrônica. O presente trabalho objetiva a caracterização das propriedades físicas e químicas das membranas de quitosana obtidas a partir da neutralização da solução policatiônica de quitosana. O trabalho foi dividido em duas etapas: solubilização e neutralização. Na primeira etapa a quitosana foi solubilizada em três concentrações diferentes de ácido acético (1%, 0.8% e 0.5%) para avaliar se a concentração de ácido exerce diferença significativa nas propriedades físico-químicas das membranas de quitosana. Na segunda etapa o policátion de quitosana foi neutralizado com duas bases fortes (NaOH e KOH) em três concentrações molares diferentes (0.5, 1 e 5 molar) pelo método de gotejamento lento da base até atingir o pH de 6.0 no policátion e obter membranas com pH perto da neutralidade. A caracterização das membranas obtidas a partir do policátion de quitosana neutralizado mostrou que as concentrações de ácido acético não mudam de forma significativa as propriedades físico-químicas das membranas. Em contraste, o processo de neutralização afetou as propriedades físico-químicas das membranas, e em particular, diferentes comportamentos foram observados dependendo da base utilizada. Membranas mais dúcteis foram obtidas após neutralização com KOH, exibindo capacidade plastificante pela base usada, enquanto que as membranas neutralizadas com NaOH apresentam um comportamento frágil. Além disso, as membranas neutralizadas com KOH exibem uma maior condução iônica em relação às propriedades elétricas das membranas, o qual pode ser interessante no desenvolvimento de biossensores ou célula combustível.
Título en inglés
Physical properties of dopped chitosan films as ionic conductors
Palabras clave en inglés
Biosensor
Chitosan
Films
Green electronics
Mechanical properties
Swelling
Transport
Resumen en inglés
The development of new materials from biodegradable elements with considerable durability, versatility and low cost is of great interest for applications in bioelectronics. The present work aims the characterization of the chemical and physical properties of chitosan membranes after neutralization of the polycation solution of chitosan. This work was divided into two steps: solubilization and neutralization. In the first step, the chitosan was solubilized with three different concentrations of acetic acid (1%, 0.8% and 0.5%) in order to evaluate whether the acid affects the physical-chemical properties of the chitosan films. In the second step, the polycation of chitosan was neutralized with two different strong bases (NaOH and KOH) using three different molar concentrations (0.5, 1 and 5), by the slow drip method of base until reaching a pH of 6.0 for the polycation and obtaining films with pH close to neutrality. The characterization of the membranes obtained from neutralized chitosan showed that the different concentrations of acetic acid did not affect the physical-chemical properties of the films significantly. In contrast, the neutralization process did affect the physical-chemical properties, and particularly, different behaviors were observed depending on the type of base used for neutralization. More ductile films were obtained after neutralization with KOH, exhibiting plastificant capacity by the used base, whereas the films neutralized with NaOH exhibited a more fragile behavior. Beyond this, regarding the electrical properties, the films with KOH presented a higher ionic conductivity, which could be interesting for developing biosensors or fuel cells.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ME7904518COR.pdf (3.40 Mbytes)
Fecha de Publicación
2014-05-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.