Disertación de Maestría
DOI
10.11606/D.74.2016.tde-08062016-113240
Documento
Autor
Nombre completo
Matheus Roberto Cabral
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2016
Director
Tribunal
Fiorelli, Juliano (Presidente)
Mendes, Rafael Farinassi
Tonin, Fernando Gustavo
Título en portugués
Painéis de partículas homogêneas cimento-bagaço de cana-de-açúcar curados por carbonatação acelerada
Palabras clave en portugués
Carbonatação
Cimento Portland
Material lignocelulósico
Painéis de cimento
Resumen en portugués
O presente estudo teve como objetivo produzir e avaliar o desempenho de painéis de partículas homogêneas de cimento-bagaço de cana-de-açúcar curados por carbonatação acelerada. Para atingir os resultados foram realizados ensaios de caracterizações morfológica e físico-química das partículas de bagaço de cana-de-açúcar, bem como ensaio de termometria para identificar a compatibilidade da matéria prima (bagaço) com o cimento. Os painéis de partículas cimento-bagaço produzidos foram submetidos a dois processos de cura distintos: 1- cura por 48 h em câmara climática, seguida por 24 h em ambiente com concentração de 15% ±0.6 de CO2, seguida por 24 dias em ambiente saturado ao ar; 2- cura em câmara climática por 48 h, seguida por 25 dias em ambiente saturado ao ar. Ao final dos 28 dias de cura e após ensaio de envelhecimento acelerado de imersão e secagem foram realizadas as caracterizações físico-mecânicas seguindo as recomendações das normativas DIN: 310; 322 e 323, bem como caracterização microestrutural e de condutividade térmica do painel de partículas cimento-bagaço. Os resultados obtidos indicaram que os painéis de partículas cimento-bagaço curados por carbonatação acelerada apresentaram melhor desempenho físico-mecânico quando comparados aos painéis não carbonatados, pois a carbonatação melhorou a interface entre as partículas e a matriz cimentícia, proporcionando maior adesividade entre as fases. E, além disso, reduziu o pH do meio alcalino em que as partículas de bagaço de cana-de-açúcar estão inseridas, minimizando o processo de degradação da lignina, celulose e hemicelulose.
Título en inglés
Particle-panels homogeneous cement bonded-bagasse cured by accelerated carbonation.
Palabras clave en inglés
Carbonation
Cement panel
Lignocellulosic material
Portland cement
Resumen en inglés
The present study aimed to produce and evaluate the performance of homogeneous particles of cement panels-bagasse-sugar cured by accelerated carbonation. To achieve the results tests were carried out morphological and physical-chemical characterization of particles of bagasse of sugar cane, as well as Thermal-test to identify the compatibility of the raw material (bagasse) with cement. The particle cement-bagasse produced were subjected to two different curing processes: 1-cure for 48 h in climate Chamber, followed by 24 h in environment with concentration of 15% ± 0.6, followed by 24 days in saturated air environment; 2-cure in climate Chamber for 48 h, followed by 25 days in saturated air environment. At the end of the 28 days of curing and after accelerated aging test of soaking and drying were realized the physical-mechanical characterizations according the recommendations of the DIN standards: 310; 322 and 323, as well as micro-structural characterization and thermal conductivity of Particleboard bagasse-cement. The results obtained indicated that the particle bagasse-cement cured by accelerated carbonation presented physical-mechanical performance better than compared with non-carbonated panels because the carbonation has improved the interface between the particles and the cementitious matrix, providing greater adhesion between phases. In addition, reduced the pH of the alkaline medium in which the particles of bagasse of sugar cane are inserted, minimizing the process of degradation of lignin, cellulose and hemicellulose.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ME8844931COR.pdf (2.71 Mbytes)
Fecha de Publicación
2016-06-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.