Doctoral Thesis
DOI
10.11606/T.74.2017.tde-22022017-105250
Document
Author
Full name
Bruno Carlos de Santis
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Pirassununga, 2016
Supervisor
Committee
Rossignolo, João Adriano (President)
Akasaki, Jorge Luís
Fioriti, César Fabiano
Morelli, Marcio Raymundo
Peruzzi, Antônio de Paulo
Title in Portuguese
Concretos leves com agregados inovadores de argila vermelha calcinada e subprodutos agroindustriais
Keywords in Portuguese
Agregado leve de alta eficiência
Agregado leve de argila calcinada
Concreto leve estrutural
Subprodutos agroindustriais
Abstract in Portuguese
Este trabalho tem por objetivo o estudo de concretos leves com agregados inovadores de argila vermelha calcinada e subprodutos agroindustriais. A argila utilizada na pesquisa foi caracterizada por meio das técnicas de limites de liquidez (LL) e plasticidade (LP), análise granulométrica, análise química e difração de raios X (DRX). Foram confeccionados corpos de prova de argila vermelha calcinada com incorporações de serragem de madeira, cinza do bagaço da cana-de-açúcar e silicato de sódio. Os corpos de prova de argila vermelha calcinada, queimados à temperatura de 900 °C, foram caracterizados por meio da avaliação da retração linear, absorção de água, porosidade aparente, massa específica aparente, expansão por umidade e resistência à compressão. Após a caracterização dos corpos de prova de argila vermelha calcinada, foram produzidos dois tipos de agregados, sendo o primeiro composto por 57% de argila e 43% de cinza do bagaço de cana-de-açúcar, conformados com água e silicato de sódio (proporção 1:1), e o segundo composto por 70% de argila e 30% de serragem de madeira. Os corpos de prova de concreto leve foram caracterizados pelos ensaios de slump, massa específica fresca, resistência à compressão, módulo de deformação, retração por secagem, absorção de água, índice de vazios e massa específica aparente e condutividade térmica. Os resultados desta pesquisa indicam a viabilidade da produção de agregados leves de argila vermelha calcinada com incorporações de subprodutos agroindustriais para utilização em concretos, uma vez que, mesmo com grande quantidade de utilização de subprodutos agroindustriais na produção dos agregados leves, os concretos produzidos com esses agregados apresentaram características similares aos concretos produzidos com agregados comerciais, apresentando um ganho econômico e energético significativo.
Title in English
Lightweight concrete with innovative calcined clay lightweight aggregates with agro-industrial by-products
Keywords in English
Agro-industrial by-products
Calcined clay lightweight aggregate
High-efficient lightweight aggregate
Lightweight concrete
Abstract in English
This paper aims to study lightweight concrete with innovative calcined clay lightweight aggregates made with agro-industrial by-products. The clay used in this research was characterized by techniques of liquid and plastic limits, particle size analysis, chemical analysis and X-ray diffraction (XRD). Calcined clay specimens were made with incorporations of wood sawdust, sugar cane ash and sodium silicate. These specimens, burned at a temperature of 900°C, were characterized by evaluating of linear shrinkage, water absorption, apparent porosity, specific mass, moisture expansion and compressive strength. After characterization of calcined clay specimens, two types of calcined clay lightweight aggregates with agro-industrial by-products were produced, wherein the first made with 57% of clay and 43% of sugar cane ash, mixed with water and sodium silicate (proportion 1:1) and the second made with 70% clay and 30% wood sawdust, mixed with water and burned at 900 °C. Specimens of lightweight concrete were characterized by slump test, fresh specific mass, compressive strength, modulus of elasticity, water absorption, voids and bulk density and thermal conductivity. Results of this research indicates the viability to produce calcined clay lightweight aggregates made with agro-industrial by-products to use in concrete, even using large amount of agro-industrial by-products, once concretes made with lightweight aggregates with agro-industrial by-products presented similar characteristics than those made with commercial aggregates, presenting significant energetic gain.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
DO7262562COR.pdf (4.03 Mbytes)
Publishing Date
2017-03-06
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.