Disertación de Maestría
DOI
https://doi.org/10.11606/D.74.2018.tde-22112018-093101
Documento
Autor
Nombre completo
Lía Ethel Velásquez Castillo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2018
Director
Tribunal
Moraes, Izabel Cristina Freitas (Presidente)
Azeredo, Henriette Monteiro Cordeiro de
Matta Junior, Manoel Divino da
Sobral, Paulo Jose do Amaral
Título en portugués
Nanocristais de amido de quinoa: produção, caracterização e aplicação em filmes de amido
Palabras clave en portugués
Casting
Chenopodium quinoa Willd
Cristalinidade
Hidrólise ácida
Nanocompósitos
Resumen en portugués
Nos últimos anos, pesquisas sobre a produção de nanocristais de amido (NCA) receberam interesse crescente devido a suas diversas aplicações, principalmente como material de reforço de matrizes poliméricas. Nesse contexto, o amido de quinoa (AQ) apresenta características desejáveis na produção de NCA tais como tamanho de grânulo pequeno e conteúdo de amilose relativamente baixo. Assim, o objetivo desta pesquisa foi produzir NCA de quinoa (NCAQ) por hidrólise ácida em diferentes temperaturas (30, 35 e 40) °C. Além disso, foi estudado o efeito da adição dos NCAQ nas propriedades estruturais e físicas de filmes de amido de mandioca. O AQ apresentou diferentes percentagens de hidrólise, no quinto dia, 63%, 73% e 91% para (30, 35 e 40) °C, respectivamente. O AQ (k = 0,59 dias-1) foi hidrolisado mais rápido que o amido de milho ceroso (k = 0,39 dias-1) a 40 °C. O rendimento dos NCAQ diminuiu com o incremento da temperatura de 30 a 40 °C; enquanto que a cristalinidade relativa dos NCAQ não foi alterada (~35%). A morfologia dos NCAQ produzidos a 30 °C foi irregular com tamanho micrométrico, enquanto que os produzidos a 35 e 40 °C apresentaram forma de paralelepípedo com tamanhos entre (50 e 100) nm e (400 e 900) nm (agregados). O diâmetro hidrodinâmico e as propriedades térmicas dos NCAQ diminuíram com o aumento da temperatura da hidrólise; enquanto que a intensidade das bandas FTIR e o potencial zeta aumentaram. As propriedades indicaram que NCAQ foram produzidos somente a (35 e 40) °C com rendimentos de 22,7% e 6,8%, respectivamente. Dessa forma, considerando o rendimento e a temperatura de transição, os NCAQ produzidos a 35 °C foram selecionados para aplicação em filmes de amido de mandioca. Os filmes foram preparados pela técnica do casting, com 4 g de amido de mandioca/100 g de dispersão filmogênica; 25 g glicerol/ 100 g de amido; e 0; 2,5; 5,0 e 7,5 g de NCAQ/ 100 g de amido. Os difratogramas de raios X confirmaram a presença dos NCAQ nos filmes. A adição de NCAQ nos filmes aumentou a rugosidade e o ângulo de contato em concentrações de 5% e 7,5%, a resistência à tração e o módulo elástico, os parâmetros de cor L* e a* em concentrações 7,5%, e a opacidade; enquanto que diminuiu a deformação na ruptura, a permeabilidade ao vapor de água na concentração de 5%, e o brilho. Outras propriedades dos filmes como espessura, umidade, solubilidade, propriedades térmicas não foram alteradas pela adição de NCAQ. Os resultados indicaram que os NCAQ produzidos a 35 °C podem ser usados como reforço em filmes nanocompósitos para melhorar suas propriedades mecânicas.
Título en inglés
Quinoa starch nanocrystals: production, characterization and application in starch films
Palabras clave en inglés
Chenopodium quinoa Willd
Acid hydrolysis
Casting
Crystallinity
Nanocomposites
Resumen en inglés
Recently researches on starch nanocrystals (SNC) production have become of interest due to their many applications, especially as reinforcement in polymeric matrices. Quinoa starch (QS) has desirable characteristics for SNC production such as small granule size and relatively low amylose content. Thus, the objective of this research was to produce quinoa SNC (QSNC) by acid hydrolysis at different temperatures (30, 35 and 40) °C. Furthermore, the effect of QSNC addition on the structural and physical properties of cassava starch films was studied. QS presented different percentages of hydrolysis on the fifth day, 63%, 73% and 91% for (30, 35 and 40) °C, respectively. QS (0.59 days-1) was hydrolyzed more rapidly than waxy maize starch (0.39 days-1) at 40 °C. QSNC yields decreased with temperature increase from (30 to 40) °C, while the relative crystallinity was not altered (~35%). The morphology of QSNC produced at 30 °C was irregular with micrometric size while those produced at 35 °C and 40 °C presented parallelepiped shapes with sizes between 50 nm and 100 nm and 400 nm to 900 nm (aggregates). The hydrodynamic diameter and the thermal properties of QSNC decreased with temperature increase, while the FTIR band intensities and the zeta potential increased. The properties indicated that quinoa QSNC were only obtained at (35 and 40) °C with yields of 22.8% and 6.8%, respectively. QSNC produced at 40 °C presented lower yield and crystallinity than waxy maize SNC, but a lower hydrodynamic diameter. Thus, based on the yield and transition temperature, QSNC produced at 35 °C was selected for application in cassava starch films. The films were prepared by casting technique, with 4 g of cassava starch / 100 g of film forming dispersion; 25 g glycerol / 100 g starch; and 0; 2.5; 5.0 and 7.5 g of QSNC / 100 g of starch. X-ray diffractograms confirmed the presence of QSNC in the films. Addition of QSNC to films increased the roughness and the contact angle at 5.0% and 7.5% concentrations, the tensile strength and elastic modulus, the color parameters L* and a* at 7.5% concentration, and the opacity; while decreasing deformation at break, water vapor permeability at 5.0% concentration, and gloss. Other film properties such as thickness, moisture content, solubility, thermal properties were not affected by QSNC addition. The results indicated that the QSNC produced at 35 ° C can be used as reinforcement in nanocomposite films to improve their mechanical properties.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ME9859279COR.pdf (3.44 Mbytes)
Fecha de Publicación
2018-11-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.