• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.74.2014.tde-30012015-150312
Documento
Autor
Nombre completo
Bruna Neri Barra
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2014
Director
Tribunal
Ghavami, Khosrow (Presidente)
Alves Júnior, Clodomiro
Frollini, Elisabete
Lahr, Francisco Antonio Rocco
Silva, Flavio de Andrade
Título en portugués
Funcionalização de fibras vegetais com plasma frio de metano para desenvolvimento de novos produtos em fibrocimento
Palabras clave en portugués
Cimento Portland
Degradação em meio alcalino
Fibras de coco verde
Fibras de sisal
Polimerização a plasma
Tratamento com plasma frio de metano
Resumen en portugués
Dentre as fibras vegetais estudadas como reforço para produção de compósitos cimentícios, as fibras de coco verde e sisal se destacam por suas características mecânicas de interesse industrial, baixo custo e baixa densidade. O objetivo deste trabalho é o estudo da funcionalização de fibras de coco verde e sisal, pela técnica de polimerização com plasma frio de metano, bem como a análise do efeito do tratamento, a fim de reduzir a hidrofilicidade natural das fibras, preservar suas propriedades mecânicas e aumentar sua durabilidade em meio alcalino. Fibras de coco verde e sisal foram tratadas com plasma frio de metano durante 4, 10 e 20 min. O experimento também incluiu ensaio de degradação das fibras, antes e após tratamento, em solução saturada de cimento Portland. Por meio de análise de molhabilidade e de espectroscopia de fotoelétrons excitados por raios X foi identificado que o tratamento tornou a superfície das fibras de sisal tratadas por 10 e 20 min menos hidrofílica, e das fibras de coco verde tratadas durante o mesmo tempo mais hidrofílica. Corroborando esses resultados, ensaio de arrancamento foi realizado em fibras de sisal tratadas por 20 min indicando boa aderência entre a fibra tratada e a matriz cimentícia. Após ensaio de degradação em solução cimentícia de ambas as fibras tratadas durante 10 e 20 min os resultados da espectroscopia na região do infravermelho por transformada de Fourier indicaram que o tratamento retardou o processo de degradação alcalina da hemicelulose e lignina das fibras de sisal, enquanto que para as fibras de coco verde a degradação das fibras sem tratamento foi igual ao daquelas sem com tratamento. Os ensaios mecânicos indicaram que as fibras de sisal tratadas tiveram maior resistência mecânica quando comparadas àquelas sem tratamento, e com relação às fibras de coco verde não houve diferença significativa entre fibras tratadas e sem tratamento. Além disso, não houve alteração do módulo de elasticidade das fibras de coco verde e sisal (sem tratamento e tratadas). Nesse contexto, os resultados obtidos indicaram que o tratamento com plasma frio de metano é eficaz para redução da hidrofilicidade da superfície das fibras de sisal, podendo vir a ser um tratamento promissor para minimizar a degradação alcalina da hemicelulose e lignina.
Título en inglés
Plasma functionalizations with methane of the vegetable fibres to development of new products in fibrocement
Palabras clave en inglés
Degradation in alkaline environment
Green coconut fibres
Methane cold plasma treatment
Plasma polymerization
Portland cement
Sisal fibres
Resumen en inglés
Among the studied plant fibres as reinforcement for the production of cement composites, green coconut and sisal fibres stand out for its mechanical characteristics of industrial interest, low cost, and low density. The aim of this work is to study of the plasma functionalization of green coconut and sisal fibres with methane cold plasma, as well as the analysis of the effect of this treatment in order to reduce the hydrophilicity of natural fibres, preserving its mechanical properties and increase its durability in alkaline medium. Green coconut and sisal fibres were treated with methane cold plasma for 4, 10 and 20 min. The experiment also included fibre degradation test before and after treatment in saturated solution of Portland cement. Wettability and XPS analyses indicated that the sisal fibres treated for 10 and 20 min presented surface more hydrophobic than green coconut fibres in the same treatment condition. Pullout test was performed in the sisal fibres treated by 20 min indicating good adherence between treated fibre and cement matrix. Both kinds of fibres were submited to degradation test imersed in the cementitious solution. The FTIR results indicated that the treatment retarded the alkaline degradation of the hemicellulose and lignin from sisal fibres whereas treated green coconut fibres showed the same degradation presented by untreated ones. The mechanical tests showed that the treated sisal fibres had higher mechanical strength compared to those without treatment, and regarding green coconut fibres there was no significant difference between treated and untreated fibres. Furthermore, there was no change in the modulus of elasticity of the green coconut and sisal fibre (treated and untreated). In this context, the results indicated that treatment with cold plasma of methane is effective in reducing the excessive hydrophilicity of the surface of sisal fibres and could be a promising treatment to minimize the alkaline degradation of hemicellulose and lignin.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DO7082311COR.pdf (2.54 Mbytes)
Fecha de Publicación
2015-02-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.