Master's Dissertation
DOI
10.11606/D.75.2010.tde-08102010-104357
Document
Author
Full name
Juliana Ramos de Andrade
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2010
Supervisor
Committee
Maule, Agnieszka Joanna Pawlicka (President)
Huguenin, Fritz Cavalcante
Nogueira, Ana Flavia
Title in Portuguese
Eletrólitos poliméricos géis à base de pectina
Keywords in Portuguese
Eletrólitos poliméricos
Impedância
Pectina
Abstract in Portuguese
Esta dissertação apresenta a preparação e caracterização de eletrólitos poliméricos géis (EPGs) a partir de pectina comercial GENU®, plastificada com glicerol e dopada com perclorato de lítio. O objetivo é a utilização de uma nova matéria-prima para a obtenção de eletrólitos poliméricos substituindo os polímeros sintéticos. A pectina é um polímero natural presente nas plantas; quimicamente é um polímero heterogêneo, e estruturalmente, é constituída unidades repetidas de (1→4)-α-D-ácido galacturônico. Os eletrólitos foram preparados usando como sal LiClO4 (0,24 g ou 30 [O]/[Li]), e 0,6 g de pectina com diferentes quantidades de glicerol (0 g - 2,0 g; 0% - 70%) como plastificante. Os filmes foram caracterizados por espectroscopia de impedância, difração de raios-X, UV-Vis, FT-IR, análises térmicas (DSC e TG). Os melhores resultados foram apresentados pelos filmes constituídos com 70% de glicerol e 30 [O]/[Li] e 68% de glicerol e 0,24 g de LiClO4. .Os filmes com 68% de glicerol apresentam valores de condutividade iônica de 1,61x10-4 S.cm-1 em temperatura ambiente aumentando para 1,72x10-3 S.cm-1 à 80°C, e uma transmitância de 80% no intervalo do visível. Os valores da energia de ativação para este filme é em torno de 37 KJmol-1. Também foi verificada a estabilidade eletroquímica em uma faixa de potencial que varia entre -1,5 a +1,5V. Os filmes com 70% de glicerol apresentam os melhores valores de condutividade iônica de 3,08x10-4 S.cm-1 em temperatura ambiente para 2,94x10-3 S.cm-1 à 80°C, e energia de ativação em torno de 35 KJmol-1, e transmitância de 75% no intervalo do visível. Os resultados obtidos indicaram que os eletrólitos a base de pectina são promissores para aplicações em dispositivos opto-eletroquimicos.
Title in English
Polymer electrolytes gel based on pectin
Keywords in English
Impedance
Pectin
Polymer electrolytes
Abstract in English
This work presents the preparation and characterization of pectin GENU®-based gel polymeric electrolytes (GPEs), plasticized with glycerol and doped with lithium perchlorate. The use of a new raw material for the production of polymeric electrolytes, as substitutes of synthetic polymers is the proposal of this work. Pectin is a natural polymer found in plants. This polymer is chemically heterogeneous and structurally, are composed of a main linear chain of (1→4)-α-D-galacturonic acid. The electrolytes were prepared using salt as LiClO4 (0.24 g or 30 [O]/[Li]) to 0.6 g of pectin and with different amounts of glycerol (0-2.0g, 0-70%) as plasticizer. The films were characterized by impedance spectroscopy, X-ray diffraction, UV-Vis, FT-IR, thermal analysis (DSC and TG). The best results were obtained with films containing 70% of glycerol and 30 [O]/[Li] and 68% of glycerol and 0.24 g LiClO4. The films with 68% of glycerol exhibit ionic conductivity values of 1.61 x10-4 S.cm-1 at room temperature with increase to1.72 x10-3 S.cm-1 at 80°C, and showed a transmittance of 80% in the visible range. The values of activation energy for this sample is around 37 kJmol-1. It was also observed the electrochemical stability in the potential range of -1.5 to +1.5 V. The films with 70% of glycerol showed best ionic conductivity values of 3.08 x10-4 S.cm-1 at room temperature wich increase to 2.94 x10-3 S.cm-1 at 80°C, and activation energy around 35 kJmol-1, and a transmittance of 75% in the visible range. All the obtained results show pectin-based polymer electrolytes over promising materials to be used in opto-electrochemical devices.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2010-12-01
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.