Tesis Doctoral
DOI
10.11606/T.75.2006.tde-11042007-143819
Documento
Autor
Nombre completo
Fabio Henrique Barros de Lima
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Ticianelli, Edson Antonio (Presidente)
Albuquerque, Hamilton Brandão Varela de
Andrade, Adalgisa Rodrigues de
Linardi, Marcelo
Perez, Joelma
Título en portugués
"Desenvolvimento de eletrocatalisadores dispersos para o cátodo de células a combustível alcalinas"
Palabras clave en portugués
células a combustível
eletrocatálise
redução de oxigênio
Resumen en portugués
A cinética da reação de redução de oxigênio (RRO) foi estudada em eletrólito alcalino em diferentes eletrocatalisadores. As atividades eletrocatalíticas medidas experimentalmente em metais puros foram correlacionadas com propriedades eletrônicas do eletrocatalisador, como o centro em energia da banda d (εd). A RRO também foi investigada em Pt e Ag modificados pela formação de liga com outros metais de transição. Por fim, a RRO foi conduzida em diferentes óxidos de manganês sintetizados em laboratório, com o objetivo de se determinar a fase mais ativa e o mecanismo da reação nos diferentes óxidos. A atividade eletrocatalítica frente à RRO dos metais puros ou das monocamadas de platina suportadas em diferentes substratos metálicos monocristalinos apresentou uma dependência tipo “vulcão” em função da energia do centro da banda d do metal eletrocatalisador. Estes resultados indicam que tanto a quebra da ligação O-O como a hidrogenação dos intermediários reacionais têm que ser facilitados, de forma que a cinética das duas reações, as quais são aceleradas por propriedades antagônicas, seja otimizada. O ganho de atividade para a RRO observado para as ligas de Pt em relação à Pt pura foi associado à menor reatividade da Pt na ligas, o que leva à uma menor força da adsorção Pt-O- e, consequentemente, maior cinética de eletroredução dos intermediários oxigenados. A maior atividade das ligas de Ag comparada com a Ag pura foi atribuída à uma mais forte adsorção Ag-O-, o que resulta em maior cinética da quebra da ligação O-O. Os resultados para os diferentes óxidos de Mn mostraram que a ativação para a RRO é maior para os materiais com alto conteúdo de MnO2. A atividade eletrocatalítica dos óxidos de manganês foi associada com um mecanismo acoplado envolvendo uma mudança do estado de oxidação de Mn (IV) para Mn (III), com a transferência de elétrons do Mn (III) para o O2 adsorvido [], em processo via 2 elétrons, com subsequente reação de desproporcionamente do intermediário HO2-, recirculando O2 no sistema, tendendo à um mecanísmo global via 4 elétrons por molécula de O2.
Título en inglés
"Developments of carbn-dispersed electrocatalysts for cathodes of alkaline fuel cells"
Palabras clave en inglés
electrocatalysis
fuel cells
oxygen reduction
Resumen en inglés
The oxygen reduction reaction (ORR) was studied on electrodes formed by Pt monolayers deposited on different metallic substrates, and on carbon-supported electrocatalysts composed by PtM/C (M = V, Cr e Co) and AgPt/C alloys, and on different Mn oxides (Mn3O4/C, Mn2O3/C and MnO2/C) in alkaline electrolyte. The experimentally measured electrocatalytic activities of the different metal catalysts and of the Pt monolayers were plotted against the metal d-band center values (_d). In all cases, the electronic features of the metal electrocatalysts were used for understanding the catalytic activities, and trying to establish the electronic/ORR kinetics relationship. The XANES results for the PtM/C alloys at high electrode potentials have shown lower vacancy of the Pt 5d band compared to pure Pt/C, indicating lower Pt reactivity for adsorbates. The enhanced catalytic activity of Pt in the alloys was attributed to a faster electroreduction of oxygenated intermediates. For the AgPt/C alloys, the XANES results have shown a emptying of the Ag orbitals due to a charge transfer to Pt, and the increased activity of the Ag atoms was ascribed to an electronic effect induced by the presence of Pt, increasing the Ag-O adsorption strength For the manganese oxide materials, the XANES results indicated a chance of the Mn oxidation state as a function of the electrode potential, and higher electrocatalytic activity was observed for MnO2/C. This was explained based on the activation for the ORR, which is higher for the material with higher MnO2 contents and the occurrence of a mediation processes involving the reduction of Mn(IV) to Mn(III), followed by the electron transfer of Mn(III) to oxygen.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2007-04-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.