Tesis Doctoral
DOI
10.11606/T.75.2006.tde-16042007-170603
Documento
Autor
Nombre completo
Roberto Batista de Lima
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Vielstich, Teresa Benita Iwasita de (Presidente)
Albuquerque, Hamilton Brandão Varela de
Olivi, Paulo
Tanaka, Auro Atsushi
Tremiliosi Filho, Germano
Título en portugués
"Estudo da eletrooxidação de etileno glicol e de seus produtos de oxidação parcial em eletrodos de Pt e PtRu"
Palabras clave en portugués
eletrodepósitos
etileno glicol
PtRu
Resumen en portugués
A eletrooxidação de etileno glicol e de seus produtos parciais de oxidação foram estudadas em eletrodos de Pt e eletrodos binários de PtRu, utilizando-se técnicas eletroquímicas fundamentais, espectroscopia de infravermelho por reflexão externa e cromatografia líquida de alta eficiência. Os resultados evidenciam um efeito catalítico na oxidação de etileno glicol com a quantidade de Ru no eletrodo até um máximo de corrente de 11mA cm-2 entre 30% a 40% em Ru. Experimentos de espectroscopia de infravermelho in situ detectaram espécies adsorvidas, como o CO, e espécies residuais contendo dois átomos de carbono. Os produtos solúveis foram glicolaldeído, ácido glicólico e CO2. Bandas bipolares de CO indicam que o etileno glicol já está totalmente dissociado no potencial de referência (0,05 V vs. RHE). Espécies contendo o grupo carbonila como o glicolaldeído também são observadas no potencial de referência (0,05 V vs RHE). A formação de CO2 é influenciada não só pela concentração do álcool em solução como também pela quantidade superficial de Ru no eletrodo. A eletrooxidação de ácido glicólico mostra a formação de CO2 a baixos potenciais (0,20 vs. RHE) e CO adsorvido a um potencial de 0,40 V.
Título en inglés
"Study of ethylene glycol electrooxidation and its partial products oxidation on Pt and PtRu electrodes"
Palabras clave en inglés
electrodeposits
ethylene glycol
PtRu
Resumen en inglés
The eletrooxidation of ethylene glycol and its partial oxidation products, glycolic acid and glycolaldehyde was studied on Pt and PtRu electrodes. Cyclic voltammetry and chronoamperometry were used for the electrochemical characterization. The nature of the reaction products and intermediates was studied by in situ Fourier transform infrared spectroscopy and high performance liquid chromatography. The oxidation reaction is catalyzed by PtRu; the maximum current density observed was 11 μA cm-2 for a ruthenium content between 30% and 40%. Adsorbed CO and residual species containing two carbon atoms as well as CO2 glycolaldehide and glycolic acid were detected by FTIR spectroscopy. Although the quantitative determination of glycolaldehyde was not possible, the results allowed an indirect estimation of this product, which starts to be formed already at 0.05V. It was found that glycolaldehyde is the main reaction product. PtRu favors the scission of the C-C bond. Thus, much higher CO coverage was found at the alloy than at pure Pt. An increase in the amount of glycolaldehyde at PtRu indicates that this material also catalyzes the scission of the C-H bond. This effect is probably due to an electronic modification of Pt caused by the presence of ruthenium, since pure Ru is not active for adsorbing or oxidizing ethylene glycol and much less Pt sites are available at PtRu.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
RobertoBatista.pdf (1.02 Mbytes)
Fecha de Publicación
2007-04-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.