Disertación de Maestría
DOI
10.11606/D.75.2006.tde-17012007-102442
Documento
Autor
Nombre completo
Fernando Cruz de Moraes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Pawlicka, Agnieszka Joanna
Romero, Jose Ricardo
Tremiliosi Filho, Germano
Título en portugués
"Influência da microestrutura dos aços inoxidáveis (austeníticos, ferríticos e martensíticos) na proteção contra a corrosão por filmes de polianilina"
Palabras clave en portugués
Aços Inoxidáveis
Corrosão
Polianilina
Resumen en portugués
Neste trabalho foram obtidos filmes de polianilina (PAni) por eletropolimerização (voltametria cíclica) sobre aços inoxidáveis austenítico (AISI 304), ferrítico (AISI 430) e martensítico (AISI 420), em meio de ácido oxálico. Os filmes de PAni foram preparados a partir de solução aquosa de ácido oxálico 0,3 mol L-1 contendo 0,1 mol L-1 de anilina a 50 mV s-1. Os valores de carga anódica total obtidos durante os estágios de eletropolimerização evidenciaram diferenças mecanísticas na polimerização da anilina sobre os diferentes aços. Os materiais poliméricos foram caracterizados por resposta eletroquímica, espectroscopias de impedância eletroquímica (EIS), de ultravioleta-visível (UV-vis-NIR), de infravermelho (IV), difração de raios X (DRX), além de microscopia eletrônica de varredura (MEV). Os filmes de PAni sobre aço AISI 420, em relação aos demais aços, apresentam diferenças significativas de morfologia. Adicionalmente, pode também ser observado que os aços com maior quantidade de cromo em sua composição, minimizam a formação de uma camada de oxalato de ferro, a qual é intermediária entre o metal e o filme de PAni. A camada de oxalato de ferro diminui as interações galvânicas entre o polímero e ferro do metal, promovendo a formação de filmes de PAni porosos e menos aderentes. A viabilidade de aplicação dos filmes de PAni dopados e desdopados, na proteção contra a corrosão dos aços inoxidáveis foi observada mediante polarização potenciodinâmica em solução aquosa de NaCl. Os parâmetros eletroquímicos extraídos das curvas demonstraram que o filme de PAni, no estado desdopado, é o que protege mais efetivamente os aços AISI 304 e AISI 430 contra a corrosão. A partir dos ensaios de corrosão e análises de EIS, foi proposto um mecanismo de deposição da PAni, o qual evidencia que a natureza do substrato metálico tem forte influência na formação dos filmes de PAni, quando a composição e a microestrutura dos aços são diferentes.
Título en inglés
"Influence of the stainless steel composition (austenitcs, martensitics and ferritcs) in the corrosion protection by polyaniline films"
Palabras clave en inglés
Corrosion
Polyaniline
Stainless Steel
Resumen en inglés
In this work were obtained polyaniline films from electropolymerization for cyclic voltammeter, on different stainless steels: (AISI-304) austenitic, (AISI-430) ferritic and martensytic (AISI-420), in oxalic acid media. PAni-films were prepared from 0.3 mol L-1 oxalic acid containing 0.1 mol L-1 aniline at 50 mV s-1. The values of total anodic charge obtained during polymerization stages demontrated difference mechanistic in the aniline polymerization on different steels. Polymeric materials were characterized for electrochemistry response and different techniques: electrochemistry impedance (EIS), ultraviolet-visible (UV-vis-NIR), infrared (IR), ray-X diffraction spectroscopes and scanning electronic microscopy (SEM). PAni films on AISI-420 steel demonstrated significant differences in the morphology, when compared another steels. Also, can be observed that the steels with chromium high content in your composition minimize the formation of iron oxalate layer, which is intermediary between the metal and PAni films. Iron oxalate layer diminishes both the galvanic interactions between the polymer and iron ions of metal and it promotes both the porous PAni films formation and lower adherence. The application viability of PAni films, in both doped and undoped states, for the protection against corrosion of stainless steels was investigated for potentiodynamic polarization in NaCl aqueous solution. The electrochemistry parameters extracted of curves demonstrated that undoped PAni films protect the AISI-304 and AISI-430 against corrosion, more effectively. With the corrosion assays and EIS analysis can be proposed a mechanism of PAni deposition, which evidence that the metallic substrate nature has strong influence on PAni films electropolymerization when both the composition and the steels microstructure differ between them.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
FernandoMoraes.pdf (8.46 Mbytes)
Fecha de Publicación
2007-01-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.