Master's Dissertation
DOI
10.11606/D.75.2008.tde-25082009-081226
Document
Author
Full name
Flávio Luiz Silva de Carvalho
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2008
Supervisor
Committee
Rodrigues Filho, Ubirajara Pereira (President)
Campana Filho, Sergio Paulo
Schneider, Jose Fabian
Title in Portuguese
Efeito da matriz no comportamento fotocrômico de ormosils de fosfotungstato
Keywords in Portuguese
filmes híbridos orgânico-inorgânicos
fosfotungstato
fotocrômicos
xerogéis
Abstract in Portuguese
Esta dissertação versa sobre o estudo de filmes híbridos orgânicos-inorgânicos do tipo ormosil com heteropoliânions do tipo Keggin. O heteropoliânion usado nesse trabalho foi: H3PW12O40 enquanto o ormosil foi obtido a partir do processo sol-gel usando tetraetilortossilicato (TEOS) como agente formador da rede 3D de silicatos e organossilanos contendo grupos oxirana e grupos básicos de Lewis nitrogenados. Realizaram-se testes do uso de Poli (dimetilsiloxano), bis (3-aminopropil) terminados (PDMSa) como agentes modificadores nos filmes. Foram obtidos filmes autossuportados e suportados em lâminas de vidro aluminossilicato. O PDMSa e o silano contendo o grupo oxirana levaram a uma queda na rugosidade média quadrática dos filmes como demonstrado nas micrografias obtidas por Microscopia Eletrônica de Varredura (MEV). Medidas de ângulos de contato estático da água sobre os filmes e de Espectroscopia de Fotoelétrons Excitados por Raios-X mostraram que há segregação do PDMSa ou do silano contendo o grupo oxirana na superfície dos filmes, entretanto os filmes com maior ângulo de contato são aqueles contendo PDMSa. Medidas de Espectroscopia de Absorção na Região do Infravermelho (IV) e Espectroscopia de Ressonância Magnética Nuclear com Rotação em Ângulo Mágico no Estado Sólido (RMN) mostraram que ormosis contendo silanos com grupo amino levam a parcial decomposição dos heteropoliânions, enquanto ormosis contendo silanos com o o grupo nitrila resultam em menor taxa de decomposição. Nos ormosis contendo igual proporção em número de moles destes dois silanos observou-se que estes dois grupos devem estar muito próximos e interagindo entre si via ligação de hidrogênio o que resultou numa queda ainda maior da taxa de decomposição. Os ormosis com silanos dotados de grupos oxirana e nitrila apresentaram maior sensibilidade a radiação UV, ou seja, a maior variação de absorbância e menor tempo de retorno à cor original. Estes filmes mostraram reprodutibilidade e não perderam sua atividade fotocrômica após serem submetidos a 10 ciclos sucessivos de irradiação com UV. Os filmes mostraram resposta linear da função de refletância com a dose de radiação UVB na faixa de 0,80 até 69 MED. Desta forma nós demonstramos a possibilidade de se obter filmes fotocrômicos reprodutíveis e estáveis e como controlar sua sensibilidade usando o processo sol-gel.
Title in English
Matriz effect in photochromic behavior of phosphotungstate ormosils
Keywords in English
hybrid organic-inorganic films
phosphotungstate
photochromic
xerogels
Abstract in English
This thesis aim to study the organic-inorganic hybrid films of the organosilanes with heteropolyanions of the Keggin type. The heteropolyanion used in this study was H3PW12O40 while the ormosil was obtained by the sol-gel process using tetraethylortossilicate (TEOS) to build the 3D silicate network and organosilanes bearing the oxirane and Basic Lewis nitrogenated groups. Poly (dimethylsiloxane), terminated with (3-aminopropyl) groups, (PDMSa) was essayed as modifiers agents in the film. The films were supported on aluminosilicate glass substrates and self-suported ones. PDMSa or oxirane bearing silanes addition results on smoother filmes reporting lower mean square root roughness based on electron micrographies obtained by Scanning Electron Microscopy (SEM). Water static contact angle measurements and X-ray Photoemission Spectroscopy (XPS) pointed out the surface segregation of the PDMSa and oxirane bearing silane, however higher contact angles were observed for the PDMSa based films. InfraRed Absorption Spectroscopy (IR) and Magic Angle Spinning Nuclear Magnetic Resonance spectroscopy (MAS NMR) results demonstrate that in ormosis with silanes bearing amino groups there was phosphotungstic acid decomposition while in ormosis with nitrile groups such decomposition is much less pronounced. For mixed ormosis with even proportion of amino and nitrile bearing silanes those functional groups are close enough to interact through hydrogen bonding resulting on even lower decomposition of the Phosphotungstate oxocluster. Those films with nitrile functional groups showed higher photochromic activity and faster bleaching time. The films showed high reproducibility and did not loose their photochromic activity after ten cycles of UV irradiation. The films bearing nitrile functionality showed linear response of the reflectance function as a function of the irradiation dose between 0,80 and 69 MED. Therefore, it was demonstrated the possibility to use sol-gel process to obtain photochromic ormosis.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2009-08-26
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.