Disertación de Maestría
DOI
https://doi.org/10.11606/D.75.2008.tde-25082009-081226
Documento
Autor
Nombre completo
Flávio Luiz Silva de Carvalho
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2008
Director
Tribunal
Rodrigues Filho, Ubirajara Pereira (Presidente)
Campana Filho, Sergio Paulo
Schneider, Jose Fabian
Título en portugués
Efeito da matriz no comportamento fotocrômico de ormosils de fosfotungstato
Palabras clave en portugués
filmes híbridos orgânico-inorgânicos
fosfotungstato
fotocrômicos
xerogéis
Resumen en portugués
Esta dissertação versa sobre o estudo de filmes híbridos orgânicos-inorgânicos do tipo ormosil com heteropoliânions do tipo Keggin. O heteropoliânion usado nesse trabalho foi: H3PW12O40 enquanto o ormosil foi obtido a partir do processo sol-gel usando tetraetilortossilicato (TEOS) como agente formador da rede 3D de silicatos e organossilanos contendo grupos oxirana e grupos básicos de Lewis nitrogenados. Realizaram-se testes do uso de Poli (dimetilsiloxano), bis (3-aminopropil) terminados (PDMSa) como agentes modificadores nos filmes. Foram obtidos filmes autossuportados e suportados em lâminas de vidro aluminossilicato. O PDMSa e o silano contendo o grupo oxirana levaram a uma queda na rugosidade média quadrática dos filmes como demonstrado nas micrografias obtidas por Microscopia Eletrônica de Varredura (MEV). Medidas de ângulos de contato estático da água sobre os filmes e de Espectroscopia de Fotoelétrons Excitados por Raios-X mostraram que há segregação do PDMSa ou do silano contendo o grupo oxirana na superfície dos filmes, entretanto os filmes com maior ângulo de contato são aqueles contendo PDMSa. Medidas de Espectroscopia de Absorção na Região do Infravermelho (IV) e Espectroscopia de Ressonância Magnética Nuclear com Rotação em Ângulo Mágico no Estado Sólido (RMN) mostraram que ormosis contendo silanos com grupo amino levam a parcial decomposição dos heteropoliânions, enquanto ormosis contendo silanos com o o grupo nitrila resultam em menor taxa de decomposição. Nos ormosis contendo igual proporção em número de moles destes dois silanos observou-se que estes dois grupos devem estar muito próximos e interagindo entre si via ligação de hidrogênio o que resultou numa queda ainda maior da taxa de decomposição. Os ormosis com silanos dotados de grupos oxirana e nitrila apresentaram maior sensibilidade a radiação UV, ou seja, a maior variação de absorbância e menor tempo de retorno à cor original. Estes filmes mostraram reprodutibilidade e não perderam sua atividade fotocrômica após serem submetidos a 10 ciclos sucessivos de irradiação com UV. Os filmes mostraram resposta linear da função de refletância com a dose de radiação UVB na faixa de 0,80 até 69 MED. Desta forma nós demonstramos a possibilidade de se obter filmes fotocrômicos reprodutíveis e estáveis e como controlar sua sensibilidade usando o processo sol-gel.
Título en inglés
Matriz effect in photochromic behavior of phosphotungstate ormosils
Palabras clave en inglés
hybrid organic-inorganic films
phosphotungstate
photochromic
xerogels
Resumen en inglés
This thesis aim to study the organic-inorganic hybrid films of the organosilanes with heteropolyanions of the Keggin type. The heteropolyanion used in this study was H3PW12O40 while the ormosil was obtained by the sol-gel process using tetraethylortossilicate (TEOS) to build the 3D silicate network and organosilanes bearing the oxirane and Basic Lewis nitrogenated groups. Poly (dimethylsiloxane), terminated with (3-aminopropyl) groups, (PDMSa) was essayed as modifiers agents in the film. The films were supported on aluminosilicate glass substrates and self-suported ones. PDMSa or oxirane bearing silanes addition results on smoother filmes reporting lower mean square root roughness based on electron micrographies obtained by Scanning Electron Microscopy (SEM). Water static contact angle measurements and X-ray Photoemission Spectroscopy (XPS) pointed out the surface segregation of the PDMSa and oxirane bearing silane, however higher contact angles were observed for the PDMSa based films. InfraRed Absorption Spectroscopy (IR) and Magic Angle Spinning Nuclear Magnetic Resonance spectroscopy (MAS NMR) results demonstrate that in ormosis with silanes bearing amino groups there was phosphotungstic acid decomposition while in ormosis with nitrile groups such decomposition is much less pronounced. For mixed ormosis with even proportion of amino and nitrile bearing silanes those functional groups are close enough to interact through hydrogen bonding resulting on even lower decomposition of the Phosphotungstate oxocluster. Those films with nitrile functional groups showed higher photochromic activity and faster bleaching time. The films showed high reproducibility and did not loose their photochromic activity after ten cycles of UV irradiation. The films bearing nitrile functionality showed linear response of the reflectance function as a function of the irradiation dose between 0,80 and 69 MED. Therefore, it was demonstrated the possibility to use sol-gel process to obtain photochromic ormosis.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-08-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.