Thèse de Doctorat
DOI
10.11606/T.75.2003.tde-14012004-152854
Document
Auteur
Nom complet
Marcio de Paula
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2003
Directeur
Jury
Goissis, Gilberto (Président)
Duek, Eliana Aparecida de Rezende
Malmonge, Sonia Maria
Plepis, Ana Maria de Guzzi
Zavaglia, Cecília Amélia de Carvalho
Titre en portugais
Compósitos colágeno aniônico : ramsana como biomateriais injetáveis : caracterização e mecanismo de interação
Mots-clés en portugais
colágeno
ramsana
reologia
viscoelasticidade
Resumé en portugais
Este trabalho descreve a preparação, caracterização e mecanismos de interação de compósitos de colágeno aniônico:ramsana, com o propósito de desenvolver géis injetáveis para correções plásticas com concentrações similares aquelas encontradas comercialmente, e sem o uso do glutaraldeído. Os materiais foram caracterizados por eletroforese, espectroscopia no infravermelho, estabilidade térmica, propriedades reológicas e ensaios de fluidez. Os materiais obtidos independentemente do processamento, são formados por colágeno não desnaturado, com preservação da estrutura secundária da proteína. Os estudos reológicos mostraram um comportamento viscoelástico para todas as preparações independentemente do pH, e com módulo de armazenamento sempre maior que o módulo de perda (G'>G" e d<45o), bem como uma maior resistência à deformação de géis de colágeno aniônico:ramsana equilibrados a pH 7,4 com relação aos géis equilibrados a pH 3,5. Medidas de viscosidade mostraram que além de um comportamento não newtoniano, a adição do polissacarídeo mesmo em baixas concentrações promove efeitos significativos sobre a viscosidade dos géis, indicando que a interação colágeno ramsana além de não comprometer a estrutura secundária do colágeno, sugere que esta interação ocorre provavelmente por ordenação da água ao redor do complexo formado. Já viscosidade dinâmica encontradas para as diferentes preparações, indicam que os compósitos obtidos são candidatos potenciais para serem utilizados em laringologia. Ensaios de fluidez mostraram que a força necessária para o escoamento de géis contendo ramsana foi sempre significativamente menor e com um perfil mais homogêneo do que aquela determinada para o colágeno aniônico, sugerindo que a associação colágeno aniônico:ramsana pode substituir com vantagens o glutaraldeído na estabilização das preparações comerciais do gel.
Titre en anglais
Anionic collagen : rhamsan composites as injectable biomateriais : characterization and interaction mechanism
Mots-clés en anglais
Collagen
rhamsan
rheology
viscoelastic
Resumé en anglais
This work describes the preparation, characterization and mechanisms of interaction anionic collagen:rhamsam composites, with the purpose of developing injectable gels for plastic corrections with similar concentrations to the commercially founded without the use of glutaraldehyde. The materials were characterized by electrophoresis, infrared spectroscopy, thermal stability, rheological properties and fluidity tests. The materials obtained independently from processing are formed by no desnaturated collagen with the preservation of secondary structure protein. The rheological studies showed a viscoelastic behavior for all the preparations independently of pH, and with storage modulus always greater than the loss modulus (G’>G’’ and d<45o), as well a higher resistence to the deformation of anionic collagen:rahamsan gels equilibrated at pH 7.4 in relation to the gels equilibrated at pH 3.5. Measure of viscosity showed that besides a non Newtonian behavior of the polysaccharide addition even at low concentrations causes significant effects on the viscosity of the gels, indicating that collagen:rhamsan interaction probably occurs due to the water disposition around the complex already formed and it does not damage the secondary structure of the collagen. On the other hand, dynamic viscosity found for different preparations indicate that the composites obtained are potential candidates to be utilized in laringology. Flow experiments indicated that the force needed for the extrusion for anionic collagen:rhamsan composites, in comparison to anionic collagen, was significantly smaller and associated with a smooth flow, suggesting that the collagen anionic:rhamsan association can substitute glutaraldehyde with advantage in the stabilization for the gels commercial preparations.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
MarciodePaula.pdf (2.04 Mbytes)
Date de Publication
2006-11-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.