Master's Dissertation
DOI
10.11606/D.75.2008.tde-18042008-164504
Document
Author
Full name
Marilia Marta Horn
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2008
Supervisor
Committee
Plepis, Ana Maria de Guzzi (President)
Assis, Odilio Benedito Garrido de
Franco, Telma Teixeira
Title in Portuguese
Obtenção e caracterização de hidrogéis de quitosana, xantana e colágeno aniônico
Keywords in Portuguese
hidrogel
quitosana
xantana
Abstract in Portuguese
Uma variedade de hidrogéis, que correspondem a uma classe de materiais poliméricos altamente hidratados está sendo empregado como biomateriais. Biopolímeros como quitosana, xantana e colágeno apresentam excelente biocompatibilidade e podem ser utilizados na área de queimados e liberação controlada de fármacos. Neste trabalho foram preparados hidrogéis provenientes da mistura entre quitosana, derivada de β-quitina, xantana comercial e colágeno aniônico (derivado de tendão bovino) em proporções variadas. A caracterização das amostras foi realizada por análise térmica (termogravimetria e calorimetria exploratória diferencial), espectroscopia no infravermelho, microscopia eletrônica de varredura e absorção de água. Pelas curvas termogravimétricas os resultados mostraram que todos os hidrogéis apresentam uma grande quantidade de água na sua estrutura e que pela reidratação são capazes de reter novamente essa quantidade de água. Por DSC observou-se que todos apresentaram o pico referente à fusão de água livre em temperaturas deslocadas acima de 0oC pelo aumento da interação água/polímero. Por FT-IR constatou-se a presença de bandas características dos biopolímeros com a ausência de novas bandas e pelo estudo por MEV os hidrogéis apresentaram uma estrutura na forma de folhas e a presença de colágeno é bastante visível participando desta estrutura.
Title in English
Chitosan:xanthan:anionic collagen hydrogels. Formulation and characterization
Keywords in English
chitosan
hydrogel
xanthan
Abstract in English
Hydrogel are polymeric materials, which have the capacity to retain a great amount of water, and are often used as biomaterials. Chitosan, xanthan and collagen present biocompatibility and they can be used in tissue regeneration and drug delivery. In this work hydrogels were prepared by the mixture with chitosan (from β-quitina), commercial xanthan and anionic collagen (from bovine tendon) in different proportions. They were characterized by thermal analysis (thermogravimetry and differential scanning calorimetry), infrared spectroscopy (FTIR), scanning electronic microscopy and water absorption. Thermogravimetric curves showed that all hydrogels present a great amount of water and after the rehydratation were capable to keep the same amount of water. Melting point of water in DSC curves were shifted to higher values due the increase of water/polymer interaction. FT-IR showed characteristic bands of biopolymers with the absence of new bands and the morphology (MEV) showed that the hydrogels structures were in sheet form and the collagen fibers are visible in the hole structure.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
MariliaMHornR.pdf (9.82 Mbytes)
Publishing Date
2008-05-21
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.