Disertación de Maestría
DOI
10.11606/D.75.2008.tde-18042008-164504
Documento
Autor
Nombre completo
Marilia Marta Horn
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2008
Director
Tribunal
Plepis, Ana Maria de Guzzi (Presidente)
Assis, Odilio Benedito Garrido de
Franco, Telma Teixeira
Título en portugués
Obtenção e caracterização de hidrogéis de quitosana, xantana e colágeno aniônico
Palabras clave en portugués
hidrogel
quitosana
xantana
Resumen en portugués
Uma variedade de hidrogéis, que correspondem a uma classe de materiais poliméricos altamente hidratados está sendo empregado como biomateriais. Biopolímeros como quitosana, xantana e colágeno apresentam excelente biocompatibilidade e podem ser utilizados na área de queimados e liberação controlada de fármacos. Neste trabalho foram preparados hidrogéis provenientes da mistura entre quitosana, derivada de β-quitina, xantana comercial e colágeno aniônico (derivado de tendão bovino) em proporções variadas. A caracterização das amostras foi realizada por análise térmica (termogravimetria e calorimetria exploratória diferencial), espectroscopia no infravermelho, microscopia eletrônica de varredura e absorção de água. Pelas curvas termogravimétricas os resultados mostraram que todos os hidrogéis apresentam uma grande quantidade de água na sua estrutura e que pela reidratação são capazes de reter novamente essa quantidade de água. Por DSC observou-se que todos apresentaram o pico referente à fusão de água livre em temperaturas deslocadas acima de 0oC pelo aumento da interação água/polímero. Por FT-IR constatou-se a presença de bandas características dos biopolímeros com a ausência de novas bandas e pelo estudo por MEV os hidrogéis apresentaram uma estrutura na forma de folhas e a presença de colágeno é bastante visível participando desta estrutura.
Título en inglés
Chitosan:xanthan:anionic collagen hydrogels. Formulation and characterization
Palabras clave en inglés
chitosan
hydrogel
xanthan
Resumen en inglés
Hydrogel are polymeric materials, which have the capacity to retain a great amount of water, and are often used as biomaterials. Chitosan, xanthan and collagen present biocompatibility and they can be used in tissue regeneration and drug delivery. In this work hydrogels were prepared by the mixture with chitosan (from β-quitina), commercial xanthan and anionic collagen (from bovine tendon) in different proportions. They were characterized by thermal analysis (thermogravimetry and differential scanning calorimetry), infrared spectroscopy (FTIR), scanning electronic microscopy and water absorption. Thermogravimetric curves showed that all hydrogels present a great amount of water and after the rehydratation were capable to keep the same amount of water. Melting point of water in DSC curves were shifted to higher values due the increase of water/polymer interaction. FT-IR showed characteristic bands of biopolymers with the absence of new bands and the morphology (MEV) showed that the hydrogels structures were in sheet form and the collagen fibers are visible in the hole structure.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MariliaMHornR.pdf (9.82 Mbytes)
Fecha de Publicación
2008-05-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.