Disertación de Maestría
DOI
10.11606/D.75.2007.tde-27032008-094508
Documento
Autor
Nombre completo
Edgar Yuji Egawa
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Plepis, Ana Maria de Guzzi (Presidente)
Polito, Wagner Luiz
Ribeiro, Clovis Augusto
Título en portugués
Caracterização térmica e reológica de blendas de glicerol:colágeno tipo I de diferentes tecidos
Palabras clave en portugués
colágeno
reologia
termogravimetria
Resumen en portugués
O colágeno possui características que fazem com seja amplamente utilizado como biomaterial. A termo-estabilidade do colágeno está diretamente relacionada a mudanças na sua estrutura (hélice tripla) via de regra quanto mais estável termicamente uma matriz, mais estável biologicamente será. Vários poliálcoois incluindo o glicerol têm apresentado um aumento na estabilidade térmica do colágeno tipo I, embora o tipo de interação não seja evidente. Este trabalho tem como objetivo estudar o efeito da adição de glicerol sobre o colágeno aniônico obtido por tratamento alcalino (24 H) em três diferentes tecidos: pericárdio e tendão bovinos e serosa porcina. Para isto são utilizados a espectroscopia na região do infravermelho (FTIR), termogravimetria e reologia. Os espectros mostraram que o tratamento alcalino e a adição de glicerol não causam desnaturação da proteína de colágeno. A partir dos resultados das curvas termogravimétricas foi observado que o glicerol aumenta a temperatura de decomposição térmica do colágeno. Os resultados dos ensaios de reologia mais precisamente a varredura de deformação mostrou que as soluções de colágeno apresentam G' maior que G'' independente do tecido de origem, e a adição de glicerol não causa mudanças nesta propriedade das soluções. A varredura de freqüência mostrou que as amostras têm características de um gel, sendo G' maior que G'' nas condições de estudo. O ensaio de escoamento a temperatura constante determinou o comportamento pseudoplástico das soluções, e a adição de glicerol causou aumento na viscosidade das soluções sem alterar tal característica. Os ensaios de escoamento com variação de temperatura permitiram determinar a temperatura de desnaturação do colágeno. A adição de glicerol aumentou apenas a temperatura de desnaturação do colágeno obtido por serosa porcina, sugerindo que esta solução é a mais sensível à adição de glicerol.
Título en inglés
Thermal and rheological characterization of glycerol: type I collagen blends
Palabras clave en inglés
collagen
rheology
thermogravimetry
Resumen en inglés
Several characteristics make collagen widely applied as a biomaterial. The collagen thermal stability is directly related with its structure changes (triple helix), generally, the better is the thermal stability the better is the biological stability. Several polyols including glycerol, has shown a increasing on type I collagen denaturation. The objective of this work is to study the effect of glycerol when mixed with anionic collagen. Type I anionic collagen was obtained after alkaline treatment (24h) of bovine pericardium, bovine tendon and porcine serosa. FT-IR, thermogravimetry and rheology were used. The results of thermal analysis showed that glycerol indeed increases the collagen decomposition temperature. The reologycal tests, precisely strain sweep, revealed that collagen samples have modulus G' prevailed on modulus G'' independent of tissue origin, and glycerol addiction did not change these. The frequency sweep revealed that collagen and collagen:glycerol samples behave like a gel-like substance since both the storage and loss modulus showed dependence with frequency sweep and G' > G'' in all cases. Flow tests at constant temperature revealed that collagen solution behave like a pseudoplastic substance, and glycerol addiction increase solution viscosity and did not change the pseudoplastic characteristic. Flow tests in function of temperature revealed collagen denaturation temperature, but glycerol addiction alters thermal stability (increase of denaturation temperature) only for collagen obtained from porcine serosa.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EdgarEgawa.pdf (1.35 Mbytes)
Fecha de Publicación
2008-03-31
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.