Disertación de Maestría
DOI
10.11606/D.75.2012.tde-01032013-141330
Documento
Autor
Nombre completo
Ricardo Bertholo Valim
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2012
Director
Tribunal
Lanza, Marcos Roberto de Vasconcelos (Presidente)
Rocha Filho, Romeu Cardozo
Santos, Mauro Coelho dos
Título en portugués
Estudo do comportamento eletroquímico de carbono Printex 6L modificado com 2-terc-butil-9,10-antraquinona e 2-etil-9,10-antraquinona para a eletrogeração de H2O2 em meio ácido
Palabras clave en portugués
eletrodos de difusão gasosa modificados
eletrossíntese
modificadores orgânicos redox
peróxido de hidrogênio
Resumen en portugués
Neste trabalho foi estudado o comportamento eletroquímico de materiais à base de carbono Printex 6L, sem e com a adição de compostos orgânicos da classe das quinonas (2-terc-butil-9,10-antraquinona (TBA) e 2-etil-9,10-antraquinona (EA)) para a produção de peróxido de hidrogênio (H2O2) a partir da reação de redução do oxigênio gasoso (O2). Na primeira etapa, foi utilizada a técnica de microcamada porosa depositada sobre um eletrodo de disco/anel rotatório, sendo que a partir dos resultados obtidos foram confeccionados eletrodos de difusão gasosa (EDG) para a eletrogeração de H2O2. Os melhores resultados utilizando a microcamada porosa foram para os materiais com a adição dos modificadores, sendo que o material com 1,0% (m/m) de TBA na demonstrou ser o mais eficiente na geração de peróxido de hidrogênio, apresentando eficiência 20% maior comparado ao Printex 6L sem modificador. Com o eletrodo de difusão gasosa confeccionado com o composto orgânico escolhido, na melhor porcentagem de adição mássica de modificador, obteve-se a concentração de 301 mg L-1, sendo que com o eletrodo confeccionado com Printex 6L sem modificador obteve-se a concentração de 175 mg L-1, sob as mesmas condições experimentais. A eficiência cinética também apresentou os mesmos resultados quanto à eficiência dos materiais escolhidos, sendo de 5,94 mg L-1 min-1 para o material com 1,0% de TBA, no potencial de -1,0 V (vs. ECS), e de 3,05 mg L-1 min-1 para o eletrodo de difusão gasosa sem modificador, no potencial de -0,8 V (vs. ECS).
Título en inglés
Study of the electrochemical behavior of carbon Printex 6L modified with 2-tert-butyl-9,10-anthraquinone and 2-ethyl-9,10-anthraquinone for electrogeneration of the H2O2 in acid medium
Palabras clave en inglés
electrosynthesis
hydrogen peroxide
modified gas diffusion electrodes
organic redox modifiers
Resumen en inglés
In this work, the electrochemistry behavior of the materials prepared with Printex 6L, with and without addition of organic compounds of the class of quinones, being the compounds: 2-tert-butyl-9,10-anthraquinone (TBA) and 2-ethyl-9,10-anthraquinone (EA). These materials were used to promote the electrogeneration of hydrogen peroxide through the oxygen reduction reaction. In the first phase, it was used the technique of porous microlayer deposited on the rotating ring/disk electrode, and after has been confectioned gas diffusion electrodes (GDE). The best results using the porous microlayer were for the materials with addition of modifiers, and the material with 1.0% (m/m) of 2-terc-butyl-9,10-anthraquinone was demonstrated to be the most efficient in generating hydrogen peroxide, presenting an efficiency 20% higher when compared to Printex 6L without the modifier. The gas diffusion electrode made with the chosen organic compound, in the best massic percentage of modifier, obtained the concentration of 301 mg L-1, and the electrode made with Printex 6L without the modifier obtained the maximum concentration of 175 mg L-1, under the same experimental conditions. The kinect efficiency also demonstrated the same results regarding the efficiency of the chosen materials, which means 5.94 mg L-1 min-1 for the material with 1.0% of 2-terc-butyl-9,10-anthraquinone, in the potential of -1.0 V(vs. SCE), and 3.05 mg L-1 min-1 for the gas diffusion electrode without the modifier, in the potential of -0.8 V (vs. SCE).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-03-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.