Tesis Doctoral
DOI
10.11606/T.75.2017.tde-30032017-091831
Documento
Autor
Nombre completo
Ricardo Bertholo Valim
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Lanza, Marcos Roberto de Vasconcelos (Presidente)
Mazo, Luiz Henrique
Mascaro, Lucia Helena
Motheo, Artur de Jesus
Olivi, Paulo
Título en portugués
Desenvolvimento e aplicação de eletrodos de difusão gasosa (EDG) modificados com óxidos bimetálicos de Ru e Nb em carbono amorfo para a eletrogeração de H2O2
Palabras clave en portugués
carbono Printex 6L
eletrodos de difusão gasosa
eletrogeração
Materiais bimetálicos
peróxido de hidrogênio
Resumen en portugués

Neste trabalho foram estudadas a atividade e seletividade de materiais bimetálicos de rutênio e nióbio, adicionados em matriz de carbono do tipo Printex 6L, para a eletrogeração de peróxido de hidrogênio a partir da reação de redução de oxigênio. Os materiais foram caracterizados por aplicação de técnicas eletroquímicas em microcamada porosa e em eletrodos de difusão gasosa, em meio ácido. Foram realizados estudos de caracterização física e morfológica dos materiais para a compreensão dos possíveis óxidos formados em substrato de carbono, por análises de difração de Raios-X, por fluorescência de Raios-X, por microscopia eletrônica de varredura acoplada a um sistema de espectroscopia de Raios-X por dispersão de energia. Por caracterização eletroquímica em microcamada porosa, o material com 5,0% de Ru05%Nb95%Oz em carbono foi escolhido como o material com maior seletividade para a eletrogeração de peróxido de hidrogênio, com eficiência de corrente calculada de 84,6%, em potencial aplicado de -0,515 V (vs. Ag/AgCl), sendo posteriormente estudado em eletrodo de difusão gasosa, por cronopotenciometria, com concentração de peróxido de hidrogênio eletrogerado de 210,74 mg L-1, em 90 minutos de experimento, com uma densidade de corrente de -100 mA cm-2, cerca de 24,5% maior quando comparada a eletrogeração de H2O2 detectada para a matriz de carbono térmico, sem adição de elementos metálicos, nas mesmas condições experimentais. Os resultados de constante cinética obtidos na mesma densidade de corrente aplicada de -100 mA cm-2, foram: de 2,44 mg L-1 min-1 para o material com 5,0% de Ru05%Nb95%Oz, e de 1,78 mg L-1 min-1 para o eletrodo de difusão gasosa sem modificador.

Título en inglés
Development and application of gas diffusion electrodes (EDG) modified with bimetallic oxides of Ru and Nb in amorphous carbon for H2O2 electrogeneration.
Palabras clave en inglés
Bimetallic materials
diffusion gas electrode
electrogeneration
hydrogen peroxide
Printex L6 carbon
Resumen en inglés

In this work, the activity and selectivity of bimetallic materials composed by ruthenium and niobium, added on carbon matrix Printex 6L, for electrogeneration of hydrogen peroxide from oxygen reduction reaction. The materials were characterized by the application of electrochemical techniques in porous microlayer and gas diffusion electrodes, in acid medium. The physical and morphological characterization were made of the materials for understanding the possible metallic oxides formation in carbon substrate by analysis of X-rays diffraction , X-rays fluorescence , by scanning electron microscopy coupled by an energy-dispersive X-ray spectroscopy. For electrochemical characterization using porous microlayer, the material with 5.0% of Ru05%Nb95%Oz in carbon was chosen as the material with greater selectivity for the hydrogen peroxide electrogeneration, with calculated current efficiency of 84.6% in applied potential of -0.515 V (vs. Ag/AgCl), studied using a gas diffusion electrode, by chronopotentiometry, with obtained hydrogen peroxide concentration of 210.74 mg L-1, at 90 minutes of experiment, with a the current density of -100 mA cm-2, about 24.5% higher when compared with the hydrogen peroxide electrogeneration detected for a carbon matrix, without addition of metal elements, under the same experimental conditions. The results obtained for calculated kinetic constant, using the same applied current density of -100 mA cm-2: 2.44 mg L-1 min-1 for using the material with 5.0% Ru05%Nb95%Oz, and 1.78 mg L-1 min-1 for using the carbon matrix without modification.

 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-03-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.