Mémoire de Maîtrise
DOI
10.11606/D.76.1995.tde-02042015-115311
Document
Auteur
Nom complet
Cesar Antonio Oropesa Avellaneda
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1995
Directeur
Jury
Aegerter, Michel Andre (Président)
Avaca, Luis Alberto
Gorenstein, Annette
Titre en portugais
Preparação e caracterização de filmes finos sol-gel de Nb2O5
Mots-clés en portugais
Não disponível
Resumé en portugais
Filmes finos de pent6xido de nióbio (Nb2O5) foram obtidos usando a técnica sol-gel a partir de sois preparados com butóxido de nióbio. Após tratamento térmico a 560°C os filmes são cristalinos (fase TT), transparentes, homogêneos e sem defeitos e rachaduras. Os filmes tem excelente propriedades eletrocrômicas com inserção de íons Li+. Eles se tornam de cor azul, com uma variação da transmissão ótica entre 80% (estado de transparência) ate 20% (estado colorido) na faixa de 300 - 1100nm. O processo de inserção e extração de Li+ é reversível e estável eletroquimicamente (testes realizados ate 2000 voltametria cíclicas). A inserção e extração de íons de Li+ foi estudada por técnica de voltametria cíclica e espectroscopia ótica num eletrólito constituído de uma solução 0,1M de perclorato de lítio (LiClO4) dissolvido em carbonato de propileno (PC). A cinética deste processos foi estudada por técnica de cronoamperometria. As caracterizações estruturais foram determinadas por difração de raios-X, retro-espalhamento de Rutheford, e espectroscopia de infravermelho. A morfologia e textura dos filmes foram estudadas usando a técnica de microscopia eletrônica de varredura (SEM)
Titre en anglais
Not availabel
Mots-clés en anglais
Not available
Resumé en anglais
Thin films of niobium. pentoxide (Nb2O5) have been obtained by sol-gel method using sols prepared from Nb pentoxide. After thermal treatment at 560°C, the coatings were found crystalline, transparent, and homogeneous without defects or cracks. The films show excellent electrochromic properties under Li+insertion. The coatings turn deep blue with a variation of the optical transmission of 80% (bleached state) to 20% (colored state) in the spectral range 300-1100nm. The process of Li+ insertion or extraction is reversible and electrochemically stable (tested up to 2000 voltammeter cycles). The electrochromic properties have been studied by electrochemical techniques such as cyclic voltammeter and optical spectroscopy in electrolyte of 0,1M lithium perclorate (LiClO4) dissolved in propylene carbonate (PC). The kinetic process was studied by chronoamperometry technique. The structural characterization has been determined by x-ray difraction, Rutherford backscattering, infrared spectroscopy. Scanning electronic micrography was used to obtain the morphology and texture of the coatings
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
CesarAvellanedaM.pdf (3.30 Mbytes)
Date de Publication
2015-04-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.