Tesis Doctoral
DOI
10.11606/T.76.2003.tde-02092010-114601
Documento
Autor
Nombre completo
Luciara Benedita Barbosa
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2003
Director
Tribunal
Andreeta, Jose Pedro (Presidente)
Baldochi, Sonia Licia
Garcia, Ducinei
Kiminami, Claudio Shyinti
Mokross, Bernhard Joachim
Título en portugués
Crescimento de fibras monocristalinas pela técnica LHPG e caracterização dos compostos Ba0,77Ca0,23TiO3, Ca2FeMoO6, CaMoO4 e SrMoO4-CaMoO4 (cristal gradiente).
Palabras clave en portugués
Ba0.77Ca0.23TiO3
Cristal gradiente
LHPG
Magnetoresistência gigante
Resumen en portugués
Este trabalho teve como finalidade determinar e otimizar as condições para a preparação e a caracterização de monocristais de alguns óxidos que apresentam considerável dependência de suas propriedades físico-químicas finais e magnitude da pressão da atmosfera de crescimento. Experimentos que envolvem diversas adaptações de um sistema de fusão a laser de pedestais foram projetados para investigar o melhor crescimento de monocristais de molibdatos alcalinos isolados e mistos (CaMoO4, cristal gradiente de CaMoO4-SrMoO4, Ca26) e de um óxido titanato alcalino (Ba0,77Ca0,23TiO3). Também, os aspectos teóricos das condições experimentais foram estudados nos termos de um modelo termodinâmico existente. Adicionalmente, é mostrado que técnicas de caracterização estruturais (curvas de rocking com raios-X, topografia de raios X, método de Rietveld), térmicas (análise térmica diferencial) e ópticas (absorção ótica) foram aplicadas com sucesso além de outros métodos de caracterização bem estabelecidos (fotografia de retro-reflexão de raios-X, análise por raios-X de elétrons retro-espalhados, microscopia eletrônica de varredura). Os experimentos e os dados das caracterizações revelam que CaMoO4, SrMoO4 e Ba0,77Ca0,23 podem ser crescidos ao ar sem alterações de suas propriedades quando tratamento térmico cuidadoso é realizado nos reagentes de partida e aos produtos, enquanto que o Ca2FeMoO6 somente pode ser crescido em atmosfera isostática de N2 e em uma faixa pequena de pressões (0,25-0,75 bar). Em qualquer caso, a estabilidade do processo de crescimento é alcançada quando gradientes térmicos específicos e relações geométricas na zona fundida são estabelecidos após a imposição de uma atmosfera adequada de crescimento. As medidas estruturais, térmicas, ópticas e de composição convencionais confirmam a formação de fases e estequiometrias desejadas. Os dados estruturais refinados e de alta resolução demonstram o controle da composição e conseqüentemente do espaçamento interplanar de rede no cristal gradiente CaMoO4-SrMoO4, um primeiro exemplo de cristal gradiente de um óxido crescido por uma técnica de zona flutuante, e abrindo um panorama largo de possibilidades para a preparação de outros cristais gradientes de óxidos.
Título en inglés
Growth of single crystal fibers by the technique LHPG and characterization of compounds Ba0,77Ca0,23TiO3, Ca2FeMoO6, CaMoO4 and SrMoO4-CaMoO4 (crystal gradient).
Palabras clave en inglés
Ba0.77Ca0.23TiO3
Giant magnetoresistance
Grandient crystal
LHPG
Resumen en inglés
This thesis examines the conditions for the optimized single crystal preparation and characterization of some oxides compounds that present high dependency of the nature and pressure magnitude of the growth atmosphere on their final physico-chemical properties. Experiments involving several adaptations to a laser-heated pedestal growth system were designed to investigate the best crystal growth of a mixed alkaline titanate oxide (Ba0,77Ca0,23TiO3) and single and mixed alkaline molybdates oxides (CaMoO4, cristal gradiente de CaMoO4-SrMoO4, Ca26). AIso, theoretical aspects of the experimental conditions were studied in terms of an existent thermodynamical model. In addition, it is shown that non-standard to techniques to characterize crystal' s structural features (X-ray rocking, X-ray topography, Rietveld's method), thermo-physical (Differential Thermal Analysis) and optical properties (Optical Absorption) were succesfully applied besides others well established characterization methods. (X-ray Laue backreflection photography, Electron Dispersive X-Ray Analysis, Scanning Electron Microscopy). Experiments and characterizations data reveal that CaMoO4, SrMoO4 e Ba0,77Ca0,23succesfully grow in air at room conditions when careful thermal treatment of the starting materiaIs and products, while Ca2FeMo06 only can be grown in isostatic atmosphere of N2/H2 (95‰ vol./5‰ voI.) and at a short pressure range (0.25-0.75 bar). In any case, the stability of the growth process is reached when specific thermal gradients and geometric relations in the meU are established after the imposition of an adequate growth atmosphere. Conventional structure, thermal, optical and composition measurements confirm the formation of desired phases and stoichiometries with excellent results for both single and mixed compounds. Refined and high resolution structural data demonstrate large control of composition and therefore interplanar lattice spacing in the gradient crystal CaMoO4-SrMoO4, a first example of an oxide gradient crystal grown by a floating zone technique, and open a wide panorama of possibilities for the preparation of novel gradient oxides crystals.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
LuciaraBarbosaD.pdf (10.04 Mbytes)
Fecha de Publicación
2010-09-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.