Dissertação de Mestrado
DOI
10.11606/D.76.1999.tde-06022014-170615
Documento
Autor
Nome completo
Luiz Fernando da Costa Zonetti
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1999
Orientador
Banca examinadora
Nunes, Luiz Antonio de Oliveira (Presidente)
Baesso, Mauro Luciano
Marega Junior, Euclydes
Título em português
Espectroscopia optica de vidros dopados com Er+3 e Yb+3
Palavras-chave em português
Espectroscopia
Laser
Terra rara
Vidros
Resumo em português
Este trabalho consiste na caracterização óptica de vidros fluoretos (fluoreto de gálio e chumbo) e de vidros óxidos (aluminato de cálcio), dopados com os íons terras raras Er+3 visando à aplicação destas matrizes como meios ativos para lasers nas regiões do infravermelho e visível. Para isto foram utilizadas as técnicas espectroscópicas de absorção óptica, luminescência, tempo de decaimento e conversão ascendente de luz. O estudo é baseado nas seguintes emissões do Er+3: 4I11/24I13/2 (2800nm), 4I13/24I15/2(1550nm) e 4S3/24I15/2(550nm). As melhores amostras óxidas para as três emissões foram aquelas codopadas com Er+3 e Yb+3. No caso dos vidros fluoretos, as amostras codopadas são mais eficientes para emissão no visível (conversão ascendente de luz) e as amostras dopadas apenas com Er+3 se mostram mais eficientes para as emissões no infravermelho. Os vidros fluoretos apresentam as maiores eficiências quânticas para as emissões de interesse devido os mesmos possuírem maior transparência e menor energia de fônons que os vidros óxidos. Porém, estes últimos apresentam maior resistência mecânica, maior condutividade e difusividade térmica o que os tornam interessantes para aplicações de alta potência. .
Título em inglês
Spectroscopy properties of glasses doped with Er+3 e Yb+3
Palavras-chave em inglês
Glass
Rare earth
Spectroscopy
Resumo em inglês
This work cansists in the optical characterization of Er+3 e Yb+3 doped fluoride, (galium and lead fluoride), and oxide, (calcium aluminate), glasses , aiming the application of theses hosts as an active media for laser in the infrared and visible regions. With this purpose we employed the spectroscopic technique of absorption and luminescence, and measurementes of excited state lifetimes and upconversion were performed. The study is based on the following Er+3: 4I11/24I13/2 (2800nm), 4I13/24I15/2(1550nm) and 4S3/24I15/2(550nm). The best oxide samples were those codoped with Er+3 e Yb+3. For the fluoride glasses, the codoped samples showed to be more eficient for emission in the visible region, (upconversion), whereas the single doped samples are more eficient for emission in the infrared region. The fluoride glasses presented larger quantic efficiency for the emissions in which we were interested, due to the fact that these glasses are more transparent and have smaller phonon energies than the oxide glasses. However, the latter have better mechanical strength, larger thermal conductivity and difusivity, which enables them to be applied in high power systems.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
LuizZonettiM.pdf (4.29 Mbytes)
Data de Publicação
2014-02-18
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.