Disertación de Maestría
DOI
10.11606/D.76.1995.tde-08112013-151141
Documento
Autor
Nombre completo
Antonio Riul Júnior
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1995
Director
Tribunal
Oliveira Junior, Osvaldo Novais de (Presidente)
Giacometti, José Alberto
Zaniquelli, Marisa Elisabete Darbello
Título en portugués
Filmes de Langmuir e Langmuir-Blodgett de polianilina processada com ácidos funcionalizados
Palabras clave en portugués
Filmes de Langmuir
Filmes Langmuir-Blodgett
Polianilina
Resumen en portugués
Filmes de Langmuir e Langmuir-Blodgett (LB) foram produzidos a partir da polianilina não substituída, que se tornou processável e solúvel em clorofórmio apos ser dopada com ácidos funcionalizados. Para atingir condições otimizadas de formação e deposição dos filmes, foi realizado um estudo criterioso empregando vários ácidos funcionalizados: canfor sulfônico (CSA), dodecilbenzeno sulfônico (DBSA) e tolueno sulfônico (TSA); e também os solventes e plastificantes N-metilpirrolidinona (NMP) e m-cresol. Soluções de polianilina de alta massa molar processada com estes ácidos foram depositadas sobre subfases aquosas ácidas (pH = 2), formando os chamados filmes monomoleculares de Langmuir. Através de um estudo dos parâmetros que influenciam a formação dos filmes de Langmuir conseguimos obter monocamadas estáveis. Desta forma os filmes puderam ser transferidos para substratos sólidos (vidro bk7), usando a técnica de Langmuir-Blodgett. Os filmes LB produzidos são do tipo Z, ou seja, a deposição só é bem sucedida na retirada do substrato, o que significa que mesmo no filme de Langmuir alguns grupos hidrofílicos se encontravam na interface filme/ar. Os filmes LB foram caracterizados por espectroscopia de UV-vis., medidas de condutividade usando o método de quatro pontas, voltametria cíclica e medidas do potencial de superfície. Os filmes LB apresentam propriedades óticas e eletroativas semelhantes as dos filmes de polianilina fabricados por centrifugação. A absorbância da banda polarônica aumenta linearmente com o número de camadas depositadas, o que demonstra que cada camada contribui com a mesma quantidade de material para o filme. A condutividade dos filmes e da ordem de 10-4 S/cm, inferior aos valores medidos para filmes obtidos por centrifugação de soluções de polianilina com CSA e DBSA, mas é maior do que a de alguns outros filmes LB de polianilina relatados na literatura
Título en inglés
Langmuir and Langmuir-Blodgett films of polyaniline processed with functionalized acids
Palabras clave en inglés
Langmuir films
Langmuir-Blodgett films
Polyaniline
Resumen en inglés
Langmuir-Blodgett (LB) films were fabricated from parent polyaniline (PANI), which was made soluble in chloroform by being doped with functionalized acids. Optimized conditions for LB film deposition were only reached after a systematic processability study in which use was made of camphor sulfonic acid (CSA), dodecylbenzene sulfonic acid (DBSA), toluene sulfonic acid (TSA) and of N-methyl pyrrolidinone (NMP) and m-cresol as plasticizers. Solutions of high molecular weight PANI were spread on acidic, aqueous subphases (pH = 2), thus forming the so-called Langmuir monolayer. These monolayer were transferred onto solid substrates (bk7 glass) in the form of Z-type films, i.e. deposition was successful only in the upstrokes. This means that hydrophilic groups must protrude from the water surface in the Langmuir film. The LB films were characterized using UV-vis spectroscopy, cyclic voltammeter, surface potential and conductivity measurements. The optical and electroactive properties of the deposited LB films were essentially the same as those obtained with spin-coated PANI films. The absorbance of the polaronic peak increases linearly with the number of deposited layers, demonstrating that each layer contributed an equal amount of material to the LB film. The films conductivity was of the order of 10-4 S/cm, which is below the values of spin coated PANI films processed with CSA or DBSA, but higher than some published values for LB films from polyaniline
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-11-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.