Antonio Carlos Bloise Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Gonzalez, José Pedro Donoso (Presidente)
Gandra, Flávio Cesar Guimarães
Magon, Claudio José
Título en portugués
Estudo por RMN de condutores iônicos poliméricos formados por blendas de POE:PEG
Palabras clave en portugués
Blendas Poliméricas
Ressonância Magnética Nuclear
Resumen en portugués
Eletrólitos poliméricos formados à partir de PIE e um sal de metal alcalino (LiBF4, LiClO4, LiCF3SO3) tem despertado grande interesse devido ao enorme potencial de aplicação em dispositivos eletroquímicos. Nestes sistemas sólidos, a macromolécula atua como solvente para o sal que fica parcialmente dissociado na matriz polimérica originando a condutividade iônica. Na tentativa de se obter complexos cada vez mais condutivos, novos sistemas tem sido propostos. Dentre eles destacam-se a formação das blendas poliméricas. Neste trabalho foram feitas investigações por Ressonância Magnética Nuclear (RMN) para se estudar a dinâmica (iônica e molecular) das blendas [POEx:PEG1-x]8LiBF4 (x=0.75, 0.50 e 0.25). Para isso realizaram-se medidas de largura de linha e taxa de relaxação dos núcleos de 1H e 19F entre - 80°C à + 80°C na freqüência de 36 MHz. Também foram feitas medidas de análise térmica (DSC) e condutividade (?). Em algumas das composições de blendas, os dados extraídos das medidas da taxa de relaxação do 1H, revelaram dinâmicas das cadeias poliméricas do POE e PEG ocorrendo separadamente. Foi observado através da análise das medidas de ressonância do 19F, que os movimentos parecem ocorrer de forma independente aos movimentos segmentários das cadeias.
Título en inglés
Study by NMR of polymeric electrolytes, based on blends of PEO:PEG
Palabras clave en inglés
Nuclear Magnetic Resonance
Polymeric blends
Resumen en inglés
Polymeric electrolytes made from POE and a alkaline metal salt (LiBF4, LiClO4, LiCF3SO3) have shown great potential in the application of electrochemical devices. In this solid systems, a macromolecule act as solvent for a salt to become partially dissociated in the polymeric matrix originating an ionic conductivity. In the attempt to obtain complexes even more conductive, new systems are proposed. Among these complexes one has distinction, polymeric blends. Investigations have been made by use of Ressonance Magnetic Nuclear (NMR), to study the ionic and molecular dynamics of this blends [POEx:PEG1-x]8LiBF4 (x=0.75, 0.50 e 0.25). For this, measurements of line width and relaxation rates of 1H and 19F in the range of -80°C to + 80°C with frequency of 36 MHz, have been done and also measurements of thermal analyse (DSC) and conductivity (?). For some blend compositions, the relaxation rate of the 1H revel that polymeric chain dynamics of POE and PEG occurs separately. It was seen by the analyse of NMR 19F measurements that the movements of the groups (BF4)- , dissociated by the polymeric matrix, seem to occur independently of the segmentary movements of the chains.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-04-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.