Mémoire de Maîtrise
DOI
10.11606/D.76.2012.tde-11012013-164115
Document
Auteur
Nom complet
Celso Donizetti de Souza Filho
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2012
Directeur
Jury
Bonagamba, Tito Jose (Président)
Caetano, Edson Passamani
Oliveira, Marcelo Falcão de
Titre en portugais
Carburização na liga HP modificada utilizada em fornos de pirólise
Mots-clés en portugais
Carburização
Liga HP modificada
Pirólise
Resumé en portugais
Os fornos de pirólise, feitos a partir da liga HP modificada, são equipamentos destinados à produção de hidrocarbonetos leves na indústria petroquímica. A partir da pirólise, é possível obter etileno e outros produtos que são matérias-primas para obtenção de manufaturados formados por polímeros. Nesse processo, grandes moléculas de hidrocarbonetos, na forma gasosa, são craqueadas em condições especiais de temperatura e pressão. Durante o craqueamento, o teor de carbono dos materiais que constituem os fornos é aumentado por meio do ingresso de carbono através da superfície interna dos tubos, sendo oriundo da massa reativa que atravessa as colunas e, como consequência disso, ocorre uma alteração das propriedades mecânicas do material. Aliado a esse fato, existe o depósito nocivo de uma camada de coque a partir da superfície interna das tubulações, que funciona como um isolante térmico, diminuindo a temperatura do gás e exigindo uma maior temperatura de trabalho para o forno, além de causar tensões que podem resultar em trincas ou danos para as colunas dos fornos de pirólise. Durante a carburização, a liga metálica dos fornos de pirólise desenvolve propriedades tipo ferromagnéticas, as quais são resultado do processo de ingresso de carbono. Nesta etapa, a camada magnetizada do material coincide com a região onde houve propagação da carburização. Sendo assim, uma medida da magnetização do material pode resultar em uma medida direta do nível de carburização em que o forno se encontra. Neste trabalho, serão apresentadas técnicas para simulação de ambientes carburizantes em alta temperatura, e as amostras serão testadas tendo o tempo de exposição ao carbono como sua principal variável e as suas propriedades mecânicas serão avaliadas, além da alteração de sua composição química e sua microestrutura.
Titre en anglais
Carburization in alloy HP modified used in pyrolysis furnaces
Mots-clés en anglais
Alloy HP modified
Carburization
Pyrolisys
Resumé en anglais
The pyrolysis heaters, made of HP-modified alloy, are equipments designed to produce lightweight hydrocarbon in the petrochemical industry. Because of the pyrolysis, it is possible to obtain ethylene and other products that are raw material to gain manufactured polymer. In this process, big gaseous hydrocarbon molecules suffer a cracking process under special conditions of temperature and pressure. During the steam cracking process, the amount of carbon from the constituent material of the heaters is increasing as a consequence of the carbon entrance through the inside surface of the tubes. This carbon comes from the reactive mass that crows the columns and, eventually, produces a change in the mechanical proprieties of the material. Besides that, there is a harmful deposit of a coke layer that comes from the internal surface of the heater tubes. This layer works as a thermal insulation and is responsible for the decreasing of the gas temperature and as a consequence, the heater demands a higher temperature to work properly. As a result, rupture or damages can occur in the pyrolysis heater columns. During the carburization, the above mentioned alloy presents magnetic properties in consequence of the increase of the carbon amount in the material. The magnetic layer is observed in the region where the carburization process happened. Therefore, a measure of the material magnetization can lead to a direct measure of the carburization level in which the heater is on. In this work, simulation techniques of the carburizing environment under high temperature will be presented, and the samples will be tested regarding the correlation between carbon exposition time and the mechanical properties, microstructural changes and chemical composition that occur as a result.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-02-08
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.