Tesis Doctoral
DOI
10.11606/T.76.2017.tde-14092017-095459
Documento
Autor
Nombre completo
Vitor Carlos Coletta
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Assaf, Elisabete Moreira
Fantini, Marcia Carvalho de Abreu
Rossi, Liane Marcia
Zanatta, Antonio Ricardo
Título en portugués
Síntese e caracterização dos compostos SrTi1-xCuxO3, CuO/SrTiO3 e NiO/SrTiO3 aplicados à catálise da reação de deslocamento gás-água
Palabras clave en portugués
Hidrogênio
Metais de transição
Reação de deslocamento gás-água
SrTiO3
Resumen en portugués
O titanato de estrôncio (SrTiO3) é um óxido de estrutura perovskita e tem sido intensamente estudado para uso em diversas aplicações, entre elas, como suporte catalítico. Entretanto, sua utilização especificamente na reação de deslocamento gás-água ainda é pouco explorada. Esta reação é de interesse para a produção de hidrogênio livre de CO, necessário para aplicações como o abastecimento de células de combustível. Este trabalho de tese teve como objetivo o estudo dos compostos SrTi1-xCuxO3, CuO/SrTiO3 e NiO/SrTiO3 como catalisadores para a reação de deslocamento gás-água, uma vez que, dentre os metais de baixo custo, Cu e Ni são altamente ativos para esta reação. As amostras SrTi1-xCuxO3 foram sintetizadas pelo método dos precursores poliméricos com calcinação em N2 e O2, possibilitando a obtenção de partículas de maior área superficial em comparação com a calcinação convencional em atmosfera ambiente. Para as amostras CuO/SrTiO3 e NiO/SrTiO3, o suporte SrTiO3, foi sintetizado pelo método de sol-precipitação e a impregnação com cobre e níquel foi realizada por via úmida. As técnicas de absorção e difração de raios-X in situ em condições de reação mostraram a estabilidade da estrutura e do estado de oxidação após o tratamento de redução. Imagens de microscopia eletrônica de varredura (MEV) e de transmissão (TEM) em conjunto com a espectroscopia de raios-X de energia dispersiva (EDX) foram utilizadas a fim de estabelecer uma relação entre a atividade catalítica e o teor a dispersão de fase ativa sobre o suporte. Todas as composições estudadas se mostraram ativas entre 250 e 350°C, entretanto, a composição NiO/SrTiO3 com 10% de Ni apresentou o melhor resultado, com uma conversão de CO a 350°C, próxima ao equilíbrio e estável por um período mínimo de10 h.
Título en inglés
Synthesis and characterization of SrTi1-xCuxO3, CuO/SrTiO3 and NiO/SrTiO3 compounds applied to catalysis of the water-gas shift reaction
Palabras clave en inglés
Hydrogen
SrTiO3
Transition metals
Water-gas shift reaction
Resumen en inglés
Strontium titanate (SrTiO3) is an oxide of perovskite structure and has been extensively studied for use in several applications, including as catalytic support. However, its use specifically in the water-gas shift reaction is still little explored. This reaction is of interest for the production of CO-free hydrogen, required for applications such as in fuel cell. This work aimed to study SrTi1-xCuxO3, CuO/SrTiO3 and NiO/SrTiO3 compounds to be applied as catalysts for the water-gas shift reaction, since, among the low-cost metals, Cu and Ni are highly active for this reaction. The SrTi1-xCuxO3 samples were synthesized by the polymeric precursor method with the samples submitted to a N2 and O2 calcination, making possible to obtain particles with a larger surface area compared to conventional calcination in ambient atmosphere. For the CuO/SrTiO3 and NiO/SrTiO3 samples, the SrTiO3 support was synthesized by the sol-precipitation method and the impregnation with copper and nickel on the support was performed by a wet method. The in situ X-ray absorption and diffraction techniques under reaction conditions showed the stability of the structure and the oxidation state after the reduction treatment. Scanning electron microscopy (SEM) and transmission (TEM) images in conjunction with energy dispersive X-ray spectroscopy (EDX) were used in order to establish a relationship between the catalytic activity and the content and dispersion of the active phase on the support. All the compositions studied were active at 250 to 350 °C, however, the NiO/SrTiO3 sample with 10% of Ni presented the best result, with a CO conversion at 350 °C, close to equilibrium and stable for a minimum of 10 h.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-09-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.