Thèse de Doctorat
DOI
10.11606/T.76.2017.tde-14092017-095459
Document
Auteur
Nom complet
Vitor Carlos Coletta
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2017
Directeur
Jury
Mastelaro, Valmor Roberto (Président)
Assaf, Elisabete Moreira
Fantini, Marcia Carvalho de Abreu
Rossi, Liane Marcia
Zanatta, Antonio Ricardo
Titre en portugais
Síntese e caracterização dos compostos SrTi1-xCuxO3, CuO/SrTiO3 e NiO/SrTiO3 aplicados à catálise da reação de deslocamento gás-água
Mots-clés en portugais
Hidrogênio
Metais de transição
Reação de deslocamento gás-água
SrTiO3
Resumé en portugais
O titanato de estrôncio (SrTiO3) é um óxido de estrutura perovskita e tem sido intensamente estudado para uso em diversas aplicações, entre elas, como suporte catalítico. Entretanto, sua utilização especificamente na reação de deslocamento gás-água ainda é pouco explorada. Esta reação é de interesse para a produção de hidrogênio livre de CO, necessário para aplicações como o abastecimento de células de combustível. Este trabalho de tese teve como objetivo o estudo dos compostos SrTi1-xCuxO3, CuO/SrTiO3 e NiO/SrTiO3 como catalisadores para a reação de deslocamento gás-água, uma vez que, dentre os metais de baixo custo, Cu e Ni são altamente ativos para esta reação. As amostras SrTi1-xCuxO3 foram sintetizadas pelo método dos precursores poliméricos com calcinação em N2 e O2, possibilitando a obtenção de partículas de maior área superficial em comparação com a calcinação convencional em atmosfera ambiente. Para as amostras CuO/SrTiO3 e NiO/SrTiO3, o suporte SrTiO3, foi sintetizado pelo método de sol-precipitação e a impregnação com cobre e níquel foi realizada por via úmida. As técnicas de absorção e difração de raios-X in situ em condições de reação mostraram a estabilidade da estrutura e do estado de oxidação após o tratamento de redução. Imagens de microscopia eletrônica de varredura (MEV) e de transmissão (TEM) em conjunto com a espectroscopia de raios-X de energia dispersiva (EDX) foram utilizadas a fim de estabelecer uma relação entre a atividade catalítica e o teor a dispersão de fase ativa sobre o suporte. Todas as composições estudadas se mostraram ativas entre 250 e 350°C, entretanto, a composição NiO/SrTiO3 com 10% de Ni apresentou o melhor resultado, com uma conversão de CO a 350°C, próxima ao equilíbrio e estável por um período mínimo de10 h.
Titre en anglais
Synthesis and characterization of SrTi1-xCuxO3, CuO/SrTiO3 and NiO/SrTiO3 compounds applied to catalysis of the water-gas shift reaction
Mots-clés en anglais
Hydrogen
SrTiO3
Transition metals
Water-gas shift reaction
Resumé en anglais
Strontium titanate (SrTiO3) is an oxide of perovskite structure and has been extensively studied for use in several applications, including as catalytic support. However, its use specifically in the water-gas shift reaction is still little explored. This reaction is of interest for the production of CO-free hydrogen, required for applications such as in fuel cell. This work aimed to study SrTi1-xCuxO3, CuO/SrTiO3 and NiO/SrTiO3 compounds to be applied as catalysts for the water-gas shift reaction, since, among the low-cost metals, Cu and Ni are highly active for this reaction. The SrTi1-xCuxO3 samples were synthesized by the polymeric precursor method with the samples submitted to a N2 and O2 calcination, making possible to obtain particles with a larger surface area compared to conventional calcination in ambient atmosphere. For the CuO/SrTiO3 and NiO/SrTiO3 samples, the SrTiO3 support was synthesized by the sol-precipitation method and the impregnation with copper and nickel on the support was performed by a wet method. The in situ X-ray absorption and diffraction techniques under reaction conditions showed the stability of the structure and the oxidation state after the reduction treatment. Scanning electron microscopy (SEM) and transmission (TEM) images in conjunction with energy dispersive X-ray spectroscopy (EDX) were used in order to establish a relationship between the catalytic activity and the content and dispersion of the active phase on the support. All the compositions studied were active at 250 to 350 °C, however, the NiO/SrTiO3 sample with 10% of Ni presented the best result, with a CO conversion at 350 °C, close to equilibrium and stable for a minimum of 10 h.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-09-29
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.