Tesis Doctoral
DOI
10.11606/T.76.1994.tde-15042014-092035
Documento
Autor
Nombre completo
Helder Nunes da Cunha
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1994
Director
Tribunal
Faria, Roberto Mendonça (Presidente)
Andrade, Adnei Melges de
Ferreira, Guilherme Fontes Leal
Giacometti, José Alberto
Livi, Rogerio
Título en portugués
Condutividade induzida por radiação-x nas fases ferroelétrica e paraelétrica em copoli(fluoreto de vinilideno/tri-fluoretileno)
Palabras clave en portugués
Condutividade induzida
Polímeros ferroelétricos
Transporte dispersivo
Resumen en portugués
O comportamento da condutividade induzida por radiação-X (RIC) em copolímeros P(VDF/TrFE) de razões molares 60/40 e 70/30 em suas fases ferroelétrica (temperatura ambiente) e paraelétrica (acima de 110°C), foi estudado para diferentes condições ambientais. Foi observado que a RIC depende fortemente sobre a conformação molecular do polímero. Variaram-se parâmetros experimentais como campo elétrico aplicado, taxa de dose, atmosfera ambiente e, principalmente a temperatura. Medidas auxiliares como correntes termoestimuladas, calorimetria diferencial, espectroscopias infravermelho, ressonância eletrônica paramagnética, difração de raios-X, etc..., deram contribuições no sentido de entender modificações estruturais e morfológicas do material devido à radiação. Para análise dos resultados da condutividade induzida (RIC), foi usado o modelo de transporte em meios dispersivos desenvolvido por Arkhipov e colaboradores. Por meio de ajustes teórico-experimentais obtivemos parâmetros importantes do material como, a mobilidade dos portadores gerados, o coeficiente de recombinação, o parâmetro dispersivo, bem como a energia de geração de pares.
Título en inglés
Radiation-induced conductivity in ferroelectric and paraelectric phases of poly(vinylidenefluoride-co-trifluoroethylene)
Palabras clave en inglés
Dispersive transport
Ferrolectric polymers
Induced conductivity
Resumen en inglés
The behavior of the radiation induced conductivity (RIC) by X-rays in P(VDF/TrFE) copolymers of 70:30 and 60:40 molar ratios, in their ferro and paraelectric phases, were studied in different environments. It was observed that the RIC depends strongly on the molecular conformation of the polymer. For the experiments several parameters were varied as the external applied field, the dose rate, the atmosphere and mainly the temperature. Auxiliar measurements as thermal stimulated currents, differential scanning calorimetry, EPR and IR spectroscopy, X-ray diffraction, etc..., were used in the sense to supply additional information about morphological and structural variations of the material due to the irradiation. For a complete analysis of the radiation induced conductivity results a dispersive transport model developed by Arkhipov et al was used. From the theoretical experimental fitting we obtained important parameters of the material: carrier mobility, recombination coefficient, dispersive parameter Q, as well as the pair-generation energy.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
HelderNunesD.pdf (6.36 Mbytes)
Fecha de Publicación
2014-04-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.