Mémoire de Maîtrise
DOI
10.11606/D.76.2012.tde-17082012-110437
Document
Auteur
Nom complet
Pedro Ivo Batistel Galiote Brossi Pelissari
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2012
Directeur
Jury
Mastelaro, Valmor Roberto (Président)
Guimarães, Francisco Eduardo Gontijo
Lisboa Filho, Paulo Noronha
Titre en portugais
Síntese e caracterização de filmes finos SrTi1-xFexO3 nanoestruturados aplicados como sensor de gás ozônio
Mots-clés en portugais
Filmes finos
Nanoestrutura
Ozônio
Perovskita
Sensor de gás
Resumé en portugais
Neste trabalho, foram desenvolvidos filmes finos de composição SrTi1-xFexO3 (0,00≤ x ≤0,150) nanoestruturados visando sua aplicação como sensor de gás ozônio. Os filmes finos foram depositados através da técnica de deposição por feixe de elétrons (EBD) cujo alvo utilizado foram pastilhas obtidas a partir do pó cristalino SrTi1-xFexO3 (0,00≤ x ≤0,150) sintetizadas através do método dos precursores poliméricos. Foi observado a partir das analises termogravimétrica e térmica diferencial que a incorporação de ferro no sistema diminui a temperatura de queima do pó precursor, sugerindo que o ferro atua como catalisador na cadeia polimérica. Os filmes depositados por DFE apresentam-se no estado amorfo sendo necessário um tratamento térmico ex-situ para que a fase cristalina desejada seja obtida. Todos os filmes apresentaram uma boa aderência aos diferentes tipos de substratos utilizados. Após o processo de cristalização, os filmes depositados sobre diferentes substratos foram caracterizados através das técnicas de difração de raios-X, espectroscopia UV-Vis e microscopia de força atômica (MFA). Foi observado que um aumento na temperatura de tratamento térmico dos filmes leva a um aumento no grau de cristalização e a uma diminuição no valor da energia de gap, calculada a partir dos espectros UV-VIS. A analise por MFA mostrou que a mudança do tipo de substrato utilizado não influencia as propriedades estruturais e microestruturais dos filmes. Através da realização de medidas de resistência elétrica, observou-se que os filmes cristalinos submetidos a um tratamento térmico ex-situ a 500oC por 4 horas apresentaram uma boa sensibilidade ao gás ozônio sendo possível detectar a presença de até 75 ppb de ozônio.
Titre en anglais
Synthesis and characterization of nanostructure SrTi1-xFexO3 thin films to be applied as ozone gas sensor
Mots-clés en anglais
Nanostructure
ozone
Ozone gas sensor
Perovskite
Thin films
Resumé en anglais
In this study, nanostructured thin films of SrTi1-xFexO3 (0.00 ≤ x ≤ 0.150) compositions were prepared looking their application as ozone gas sensor. The thin films were deposited using the technique of electron beam deposition (EBD) whose targets were obtained from polycrystalline SrTi1-xFexO3 (0.00 ≤ x ≤ 0.150) powders synthesized by the polymeric precursor method. It was observed from the thermogravimetric and differential thermal analysis that the incorporation of iron in the system decreases the calcination temperature of the precursor powders, suggesting that the iron acts as a catalyst in the polymer chain. The as obtained films deposited by EBD present an amorphous state being necessary a ex-situ heat treatment to obtain the desired crystalline phase. All films showed good adhesion to different substrates. After the crystallization process, the films deposited on different substrates were characterized through X-ray diffraction, UV-Vis spectroscopy and atomic force microscopy (AFM) trechniques. It was observed that an increase in the annealing temperature of the film results in an increase in the degree of crystallization and a decrease in the value of band gap energy, which was calculated from the UV-VIS spectra. The AFM analysis showed that changing the type of substrate does not influence the structural properties and microstructure of the films. By carrying out measurements of electrical resistance, it was observed that the crystalline films subjected to a ex-situ heat treatment at 500oC for 4 hours showed a good sensitivity to the ozone gas being possible to detect the presence of up to 75 ppb ozone.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-08-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.