Thèse de Doctorat
DOI
10.11606/T.76.2000.tde-21022014-164628
Document
Auteur
Nom complet
Dione Fagundes de Sousa
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2000
Directeur
Jury
Nunes, Luiz Antonio de Oliveira (Président)
Bagnato, Vanderlei Salvador
Guimarães, Francisco Eduardo Gontijo
Messaddeq, Younes
Ribeiro, Sidney José Lima
Titre en portugais
Estudo espectroscópico de vidros fluoretos e óxidos dopados com Er3+:Yb3+ e Tm3+:Ho3+
Mots-clés en portugais
Espectroscopia óptica
Vidros
Resumé en portugais
Neste trabalho foram estudadas duas composições vítreas, a saber: 30PbF2 - 15InF3 - 20GaF3 - 15ZnF2 - 20CaF2, chamada fluoroindogalato e 41,5Al2O3 - 47,4CaO - 7SiO2 - 4,1MgO, chamada LSCA ( do inglês Low Silica content Calcium Aluminate). A matriz de fluoroindogalato foi dopada com dois conjuntos de íons terras-raras: Tm3+ + Ho3+ e Er3++Yb3+, enquanto que a matriz LSCA foi dopada apenas com os íons Er3+:Yb3+. O objetivo do trabalho foi a caracterização destas matrizes como possíveis meios ativos para laser de estado sólido nas regiões de 2,0 µm (Ho3+) e 2,8µm (Er3+). Neste sentido, foram realizados os experimentos de absorção óptica, fotoluminescência e tempo de vida. A partir dos dados obtidos, foram calculados os parâmetros de intensidade de Judd-Ofelt, os microparâmetros de transferência de energia e o coeficiente de ganho óptico das transições eletrônicas 5I75I8 (Ho3+) e 4I11/24I13/2 (Er3+). A contribuição deste trabalho a espectroscopia de terras-raras em vidros está na caracterização destes íons em termos dos parâmetros de transferência de energia via os modelos de Dexter e Yokota e Tanimoto. Haja vista que tais dados não se encontram disponíveis na literatura especializada. Os resultados mostraram que ocorrem processos de transferência de energia de ordem mais alta que dipolo-dipolo nas interações Tm3+→ Tm3+ e Tm3+→ Ho3+. A transição 5I75I8 do Ho3+ apresenta coeficiente de ganho óptico positivo a partir da densidade de excitação de 1,2 kW/cm2. Os processos de transferência de energia Er3+→ Er3+ e Er3+→ Yb3+ ocorrem via mecanismo de dipolo-dipolo e a transição 4I11/24I13/2 do Er3+ não é auto-terminada na matriz de fluoroindogalato. O coeficiente de ganho óptico para esta transição é sempre positivo para qualquer densidade de excitação. . A matriz LSCA apresenta auto-terminação da transição 4I11/24I13/2 do Er3+, sendo portanto, necessária a inserção dos mecanismos de upconversion para a observação de ganho óptico nesta transição eletrônica
Titre en anglais
Spectroscopy próperties of fluoride and oxides doped with Er3+:Yb3+ and Tm3+:Ho3+
Mots-clés en anglais
Glass
Rare earth
Spectroscopy
Resumé en anglais
In this work two vitreous compositions were studied, that are: fluoroindogalate (30PbF2 - 15InF3 - 20GaF3 - 15ZnF2 - 20CaF22) and LSCA (41,5Al2O3 - 47,4CaO - 7SiO2 - 4,1MgO) - Low Silica Content Calcium Aluminates. The fluoroindogalate host was doped with two sets of rare earth ions: Tm3+ + Ho3+ and Er3++Yb3+, whereas the LSCA host was only doped with Er3+ and Yb3+ ions. The aim of the work was the characterization of these hosts as possible active media for solid state lasers in the spectral regions of 2,0 µm (Ho3+) and 2,8µm (Er3+). In this sense, optical absorption, photoluminescence and lifetime experiments were performed. From the resulting data, Judd-Ofelt intensity parameters, energy transfer microparameters and the electronic transitions 5I75I8 (Ho3+) and 4I11/24I13/2 (Er3+) optical gain coefficients were calculated. This work's contribution to the rare earth spectroscopy lies in the characterization of such ions in terms of the energy transfer parameters using the Dexter, and Yokota and Tanimoto models considering that these data are not available in the specialized literature. The results have shown that higher than dipole-dipole order processes occur in the interactions Tm3+→ Tm3+ and Tm3+→ Ho3+. The Ho3+ 5I75I8 transition presents positive optical gain coefficient starting from the excitation density of 1.2 kW/cm2. The energy transfer processes Er3+→ Er3+ and Er3+→ Yb3+ occur via dipole-dipole mechanism and the Er3+ 4I11/24I13/2 transition is not auto terminated in the fluoroindogalate host. The optical gain coefficient for this transition is always positive for any excitation density. The LSCA host presents auto termination of the Er3+ 4I11/24I13/2 making it necessary the insertion of upconversion mechanisms for the observation of the optical gain in this electronic transition
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
DioneSousaD.pdf (9.30 Mbytes)
Date de Publication
2014-03-11
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.