Tesis Doctoral
DOI
10.11606/T.76.2010.tde-22102010-134405
Documento
Autor
Nombre completo
Higor Rogerio Favarim
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Briois-Labarbe, Valérie
Michalowicz, Alain
Pereira-Ramos, Jean Pierre
Pulcinelli, Sandra Helena
Título en portugués
Síntese, caracterização elétrica e estrutural de cerâmicas ferroelétricas de composição Ba0,90R0,10Ti1-xZrxO3 (R=Ca, Sr)
Palabras clave en portugués
Cerâmicas ferroelétricas
Difração de raios X
Espectroscopia de absorção de raios X
Espectroscopia de impedância
Resumen en portugués
O presente trabalho teve como objetivo o estudo das propriedades elétricas e estruturais das amostras cerâmicas pertencentes ao sistema Ba1-xRxTi1-yZryO3 (R=Ca,Sr). As amostras na forma de pó micro ou nanoestruturadas foram respectivamente obtidas através do método de mistura de óxidos e do método dos precursores poliméricos. Amostras cerâmicas apresentando grãos em uma escala micrométrica foram obtidas através do método tradicional de sinterização em alta temperatura enquanto amostras cerâmicas nanoestruturadas foram obtidas através da técnica de sinterização por plasma (Spark plasma Sintering ou SPS). Os resultados obtidos através da técnica de espectroscopia de impedância mostraram que com o aumento da quantidade de Zr na matriz as amostras passam de um estado ferroelétrico normal para um estado ferroelétrico relaxor e que este efeito é mais pronunciado nas amostras contendo cálcio. A partir dos resultados da difração de raios X em alta resolução, foi possível determinar os processos de transição de fase em função da substituição dos átomos de Ti por Zr além de identificar um processo de transição de fase espontânea na amostra contendo cálcio e 18 mol % de zircônia. Através das medidas do espectro de absorção de raios X e do espectro Raman foi possível mostrar que, independente da composição e da estrutura a longa distancia, apresentam certo grau de desordem local e que esta desordem local está principalmente associada ao fato do átomo de titânio estar fora de sua posição centro simétrica no octaedro TiO6 e que está desordem é comparável a observada no composto BaTiO3 tetragonal. A desordem química devido ao aumento da quantidade de átomos de Zr na matriz associada a esta desordem local levam ao aparecimento do estado relaxor. Finalmente, o estudo das amostras preparadas por SPS mostraram que é possível obter amostras de composição BaTi0,80Zr0,20O3 apresentando uma alta densidade e tamanho de grão nanométrico. Os resultados da espectroscopia de impedância destas amostras mostraram devido ao pequeno deslocamento da temperatura de máximo e do alargamento da curva de permissividade com a diminuição do tamanho de grão, não foi possível classificar essa amostra como apresentando um comportamento típico de um material ferroelétrico relaxor.
Título en inglés
Synthesis, electric and structural characterization of Ba0,90R0,10Ti1-xZrxO3 (R= Ca, Sr) ferroelectric ceramic system
Palabras clave en inglés
Ferroelectric ceramics
Impedance spectroscopy
X-ray absorption spectroscopy
X-ray diffraction
Resumen en inglés
This work aimed to study the structural and electrical properties of ceramic samples belonging to the Ba1-xRxTi1-yZryO3 (R = Ca, Sr) system. The powder samples presenting a micro or nanosize were respectively obtained by using a mixture of oxides and by the modified polymeric precursor methods. Micrometer scale ceramic samples were obtained through the traditional method of sintering at high temperature while nano-sized particles ceramics were obtained using the spark Spark Plasma Sintering (SPS) technique. The results obtained using the technique of impedance spectroscopy showed that with an increasing amount of Zr in the matrix, samples change from a normal ferroelectric state to a relaxor ferroelectric state and that this effect is more pronounced in samples containing calcium. From the results of high resolution X-ray diffraction technique, it was possible to determine the phase transition processes due to the substitution of Ti atoms by Zr and, in addition, identify a process of spontaneous phase transition in the sample containing calcium and 18 mol% of zirconium. From the measurements of X-ray absorption Spectroscopy and Raman spectra it was possible to show that regardless of the composition and structure of long range order, the samples have some degree of local disorder and that this local disorder is primarily associated with the fact that the titanium atom being out of its symmetrical center position in the octahedron and is TiO6 disordered. This is comparable to the distorsion observed in tetragonal BaTiO3 sample. The chemical disorder due to the increase of Zr atoms in the matrix associated with this disorder is responsible of the occurrence of relaxor state. Finally, the study of samples prepared by SPS showed that it is possible to obtain samples with BaTi0,80Zr0,20O3 composition with a high-density and nanometeric grain size. The results of impedance spectroscopy on these samples show a small shift of the maximum temperature and a slight broadening of the permittivity curve with decreasing grain size. However, this result does not allowed to classify the samples as having a typical relaxor ferroelectric material behavior.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-10-28
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • Favarim, Higor R., et al. Phase-transition studies of Ba0.90Ca0.10(Ti1?xZrx)O3 ferroelectric ceramic compounds [doi:10.1002/pssa.201026242]. Physica Status Solidi. A, Applications and Materials Science [online], 2010, vol. 207, p. 2570-2577.
  • Favarim, Higor R., et al. Short-Range Structure of Ba0.90Ca0.10Ti1-xZrxO3 Ferroelectric Ceramic Compounds probed by XAS and Raman Scattering Techniques. In 12th European Meeting on Ferroelectricity, Bordeaux, 2011. Procedings of the 12th European Meeting of Ferroelectricity., 2011. Abstract.
  • Mastelaro, V R, et al. Structure of Ba0.90Ca0.10Ti1-xZrxO3 Ferroelectric ceramic compounds probed by multiedge x-ray absorption spectroscopy. In X SBPmat, Gramado, 2011. resumos da X SBPmat., 2011. Resumo.
  • MASTELARO, V. R., et al. Nanocrystalline Ferroelectric BaTi0.80Zr0.20O3 ceramic prepared by spark Plasma sintering. In 2011 MRS Fall Meeting, Boston, USA,, Boston, 2011. Resumos do 2011 MRS Fall Meeting., 2011. Abstract.
  • MASTELARO, V. R., et al. Structural and dielectric characterization of Ba0,9Sr0,1ZrxTi1-xO3 system. In 20a Reuniao anual de usuarios do LNLS (RAU), Campinas, 2010. resumos da 20a Reuniao anual de usuarios do LNLS (RAU). : LNLS, 2010. Resumo.
  • Mastelaro, Valmor R., et al. XAS versus XRD studies of Ba0.90Ca0.10Zr1-xTixO3 Ferroelectric Materials. In 14th International Conference on X-ray Absorption Fine Structure, Camerino, Italia, 2009. Proceedings of the 14th International Conference on X-ray Absorption Fine Structure., 2009. Abstract.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.