Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Daniela Vieira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2018
Director
Tribunal
Yoshioka, Sérgio Akinobu (Presidente)
Lucas, Alessandra de Almeida
Ramírez Gil, Miguel Ángel
Salomão, Rafael
Título en portugués
Obtenção e caracterização de biocompósitos formados a partir de hidroxiapatita sintética e fibroína de seda na forma de blocos para enxerto ósseo
Palabras clave en portugués
Biocompósito
Engenharia de tecido
Fibroína de seda
Hidroxiapatita
Regeneração óssea
Resumen en portugués
Biomateriais que promovem e auxiliam a regeneração óssea vêm ganhando grande visibilidade em pesquisas na área de engenharia tecidual, em destaque os biocompósitos a partir de cerâmicas e polímeros. Muitos desafios abrangem essa área de pesquisa, sendo o principal, criar um material que mais se assemelha ao osso, não só em sua resistência mecânica, mas também em sua bioatividade e porosidade. Esse projeto tem como foco o desenvolvimento e processamento de blocos de biocompósito formados a partir de hidroxiapatita (HAp) e fibroína de seda (FS). A fibroína de seda, obtida a partir dos casulos do bicho-da-seda, foi lavada em solução de carbonato de sódio com concentração de 5% por 30 minutos. Sua dissolução foi realizada através de solução ternária contendo cloreto de cálcio, etanol e água, na proporção molar de 1:2:8. A HAp foi co-precipitada na FS dissolvida em solução ternária através de solução de fosfato (Na2HPO4) sob agitação constante. Os blocos foram prensados manualmente e avaliou-se sua morfologia, relação Ca/P e absorção de líquido definindo a melhor proporção de %HAp e %FS. Após a determinação da proporção 75%HAp e 25% FS, os blocos foram conformados em prensa hidráulica com pressões fixas de 50 e 100 MPa. As características morfológicas foram avaliadas através de análises de MEV, porosidade, absorção de líquidos, microtomografia computadorizada (?-CT) e medição da área superficial específica (BET). As características químicas e estruturais foram analisadas por EDS, FTIR, TGA e DRX. Além disso, avaliou-se a resistência à compressão, a bioatividade e a citotoxicidade do biocompósito. Os resultados mostram que o biocompósito estudado apresenta características químicas e estruturais próxima ao osso trabecular, resistência à compressão entre 2 e 10 MPa e porosidade entre 30% e 70%, é biocompatível e possui capacidade de formação de apatita. O biomaterial em estudo apresenta-se como uma boa perspectiva na área de engenharia tecidual óssea.
Título en inglés
Obtainance and characterization of biocomposites prepared from synthetic hydroxyapatite and silk fibroin in form of blocks for bone grafting
Palabras clave en inglés
Biocomposite
Bone regeneration
Hydroxyapatite
Silk fibroin
Tissue engineering
Resumen en inglés
Biomaterials that promote and aid bone regeneration have gained great visibility in tissue engineering research, with emphasis on biocomposites from ceramics and polymers. Many challenges cover this area, the main is being to create a material similar to bone, not only in its mechanical strength but also in its bioactivity and porosity. This project focuses on the development and processing of biocomposite blocks formed by hydroxyapatite (HAp) and silk fibroin (SF). The silk fibroin, obtained from the cocoons of the silkworm, was washed in 5% sodium carbonate solution for 30 minutes. Its dissolution was carried out through a ternary solution containing calcium chloride, ethanol and water, in a molar ratio of 1: 2: 8. The HAp was co-precipitated in SF dissolved in ternary solution through phosphate solution (Na2HPO4) under constant stirring. The blocks were manually pressed and their morphology, Ca/P ratio and liquid absorption were evaluated to determine the best HAp/FS ratio. After defined the best ratio, 75%HAp and 25% FS, blocks were formed in a hydraulic press with fixed pressures (50 and 100 MPa). The morphological characteristics were evaluated by SEM, Porosity, Liquid Absorption, Computerized Microtomography (?-CT) and specific surface area (BET). The chemical and structural characteristics were analyzed by EDS, FTIR, TGA and XRD. In addition, the compressive strength, bioactivity and cytotoxicity of the composite were evaluated. The results show a biocomposite with chemical and structural characteristics close to the trabecular bone, mechanical resistance between 2 and 10 MPa and porosity between 30% and 70%, it is biocompatible and with apatite formation capacity. The biomaterial studied presents a good perspective in the field of bone tissue engineering.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-05-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.