Disertación de Maestría
DOI
10.11606/D.82.2017.tde-24102017-120530
Documento
Autor
Nombre completo
Maria Fernanda do Carmo Gurgel
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Goissis, Gilberto (Presidente)
Crnkovic, Ovidio Richard
Plepis, Ana Maria de Guzzi
Título en portugués
Preparação e caracterização de mantas colágeno aniônico: hidroxiapatita para reconstrução de tecido ósseo
Palabras clave en portugués
Biocerâmica
Biomateriais
Resumen en portugués
O principal objetivo deste trabalho foi a preparação e a caracterização de mantas obtida na mistura de colágeno aniônico e HA particulada para aplicação como biomaterial, com a finalidade de minimizar os problemas de espalhamento que ocorre com as biocerâmicas convencionais. Sua principal vantagem é a fácil manipulação para fins de reconstrução de tecido ósseo. Os materiais de partida utilizados foram colágeno aniônico extraído do tendão bovino, hidroxiapatita não estequeométrica (nHA) e Osteosynt (40-60 rnesh)- HA e, a partir destes materiais, três tipos de cornpósitos na forma de mantas foram preparados pela mistura colágeno aniônico: HA, colágeno aniônico:nHA, colágeno aniônico:HA:nHA. A HA e nHA também foram submetidas a análise da razão Ca/P por espectrofotometria de absorção atômica para a determinação de cálcio e espectofotometria de UV no visível para fósforo. Análise da razão cálcio/fósforo para nHA e HA indicou que a hidroxiapatita sintetizada é deficiente em cálcio, com razão Ca/P de 1,58 comparada com HA de razão Ca/P de 1,67. Segundo os resultados de caracterização por IV, DSC e DRX dos materiais de partida e das mantas, no caso, da HA e da nHA, o IV e o DRX mostraram características similares às da literatura e os de DSC indicaram que o processo de mistura para se obter as mantas não induz a desnaturação da estrutura do colágeno. O DRX e IV mostraram que as características originais da HA e nHA bem como a do colágeno permaneceram.
Título en inglés
not available
Palabras clave en inglés
not available
Resumen en inglés
The major aim of this work is the preparation and characterization of composites obtained by mixture of anionic collagen and powdered HA for the use as biomaterial, in order to minimize scattering problems which are common in conventional bioceramics. The main advantage of this composite is the easy handling in the bone reconstruction. The used materials were anionic collagen extracted of bovine tendon, non-stoichometric hydroxyapatite (n-HA) and Osteosynt® ( 40-60 mesh)-HA. Using these materials, we obtained three composites by mixing anionic collagen:HA, anionic collagen:n-HA and anionic collagen:HA:n-HA. All materials were characterized by infrared spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) and X-Ray Difraction (XRD). The Ca/P ratio was obtained for HA and n-HA, using atomic absorption for calcium determination and UV-Vis spectrofotometry for phosphorus. The Ca/P ratio indicated that synthesized hydroxyapatite is calcium deficient (1.58) as compared with commercial HA Ca/P ratio (1.67). The characterization results obtained by IV and XRD showed similar characteristics to the literature and DSC data indicated that the process mixing to obtain composites did not induce collagen denaturation. XRD and IV data showed that original characteristics of HA and n-HA were maintened.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-10-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.