Mémoire de Maîtrise
DOI
10.11606/D.82.2017.tde-24102017-120530
Document
Auteur
Nom complet
Maria Fernanda do Carmo Gurgel
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2000
Directeur
Jury
Goissis, Gilberto (Président)
Crnkovic, Ovidio Richard
Plepis, Ana Maria de Guzzi
Titre en portugais
Preparação e caracterização de mantas colágeno aniônico: hidroxiapatita para reconstrução de tecido ósseo
Mots-clés en portugais
Biocerâmica
Biomateriais
Resumé en portugais
O principal objetivo deste trabalho foi a preparação e a caracterização de mantas obtida na mistura de colágeno aniônico e HA particulada para aplicação como biomaterial, com a finalidade de minimizar os problemas de espalhamento que ocorre com as biocerâmicas convencionais. Sua principal vantagem é a fácil manipulação para fins de reconstrução de tecido ósseo. Os materiais de partida utilizados foram colágeno aniônico extraído do tendão bovino, hidroxiapatita não estequeométrica (nHA) e Osteosynt (40-60 rnesh)- HA e, a partir destes materiais, três tipos de cornpósitos na forma de mantas foram preparados pela mistura colágeno aniônico: HA, colágeno aniônico:nHA, colágeno aniônico:HA:nHA. A HA e nHA também foram submetidas a análise da razão Ca/P por espectrofotometria de absorção atômica para a determinação de cálcio e espectofotometria de UV no visível para fósforo. Análise da razão cálcio/fósforo para nHA e HA indicou que a hidroxiapatita sintetizada é deficiente em cálcio, com razão Ca/P de 1,58 comparada com HA de razão Ca/P de 1,67. Segundo os resultados de caracterização por IV, DSC e DRX dos materiais de partida e das mantas, no caso, da HA e da nHA, o IV e o DRX mostraram características similares às da literatura e os de DSC indicaram que o processo de mistura para se obter as mantas não induz a desnaturação da estrutura do colágeno. O DRX e IV mostraram que as características originais da HA e nHA bem como a do colágeno permaneceram.
Titre en anglais
not available
Mots-clés en anglais
not available
Resumé en anglais
The major aim of this work is the preparation and characterization of composites obtained by mixture of anionic collagen and powdered HA for the use as biomaterial, in order to minimize scattering problems which are common in conventional bioceramics. The main advantage of this composite is the easy handling in the bone reconstruction. The used materials were anionic collagen extracted of bovine tendon, non-stoichometric hydroxyapatite (n-HA) and Osteosynt® ( 40-60 mesh)-HA. Using these materials, we obtained three composites by mixing anionic collagen:HA, anionic collagen:n-HA and anionic collagen:HA:n-HA. All materials were characterized by infrared spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) and X-Ray Difraction (XRD). The Ca/P ratio was obtained for HA and n-HA, using atomic absorption for calcium determination and UV-Vis spectrofotometry for phosphorus. The Ca/P ratio indicated that synthesized hydroxyapatite is calcium deficient (1.58) as compared with commercial HA Ca/P ratio (1.67). The characterization results obtained by IV and XRD showed similar characteristics to the literature and DSC data indicated that the process mixing to obtain composites did not induce collagen denaturation. XRD and IV data showed that original characteristics of HA and n-HA were maintened.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-10-24
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.