Mémoire de Maîtrise
DOI
10.11606/D.85.2013.tde-06062013-090450
Document
Auteur
Nom complet
Eduardo Gurzoni Alvares Ferreira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2013
Directeur
Jury
Marumo, Júlio Takehiro (Président)
Gobbo, Luciano de Andrade
Vicente, Roberto
Titre en portugais
Avaliação da alteração das propriedades da pasta de cimento em ambiente de repositório
Mots-clés en portugais
durabilidade
pasta de cimento
rejeitos radioativos
repositório
Resumé en portugais
Pasta de cimento é um material comum em repositórios para rejeitos radioativos, atuando como material estrutural e de imobilização. Sua utilização como material de preenchimento em um repositório tipo poço tubular profundo para fontes seladas, no entanto, requer um maior tempo de vida útil do material. O conhecimento de seu comportamento em longo prazo é necessário para garantir a segurança da instalação em milhares de anos. O presente trabalho avaliou as alterações na pasta de cimento induzidas por fatores de degradação, como ataque de agentes agressivos, alta temperatura e presença de campo de radiação. Corpos de prova (cps) de pasta de cimento foram submetidos a ensaios acelerados de degradação e os efeitos deletérios foram avaliados por meio de ensaios de resistência mecânica, variação dimensional, lixiviação/penetração de íons, DRX, TGA e MEV. Observou-se que a hidratação dos cps foi beneficiada pela imersão (em água destilada ou em solução salina) e alta temperatura, resultando em uma resistência maior. O armazenamento à seco prejudicou a hidratação, mantendo a resistência mais baixa. O tempo de imersão e a irradiação não foram capazes de alterar a mineralogia e a resistência da pasta de cimento.
Titre en anglais
Assessment of cement paste properties changes in repository environment
Mots-clés en anglais
cement paste
durability
radioactive waste
repository
Resumé en anglais
Cement paste is widely used in repositories for radioactive wastes, acting as structural and immobilization material. However, its use as backfill material in boreholes for sealed sources requires a longer service life of this material. The assessment of the cement paste behavior in long term is needed to improve the confidence that the material will perform as required during the service life of the facility. This research evaluated the changes in cement paste induced by degradation parameters. Portland cement paste specimens (cps) were submitted to accelerated degradation tests and the damage effects was evaluated by mechanical strength, variation of sample mass and volume, leaching/penetration of ions, XRD, TGA and SEM. It was observed that cps hydration was benefited by immersion (in distilled water or salt solution) and high temperatures, resulting in a higher strength. Dry storage, however, influenced the hydration process and maintained strength lower. Time of treatment and irradiation were not able to alter mineralogy and durability of cement paste.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-07-30
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.