Tesis Doctoral
DOI
10.11606/T.85.1999.tde-06112003-182641
Documento
Autor
Nombre completo
Hugo David Chirinos Collantes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1999
Director
Tribunal
Osso Júnior, João Alberto (Presidente)
Guedes, Selma Mateus Loureiro
Mei, Lucia Helena Innocentini
Taqueda, Maria Elena Santos
Villarreyes, Joaquin Ariel Moron
Título en portugués
Desenvolvimento do Processo de Fabricação de Tubos Hospitalares por RVNRL: Otimização e Protótipo de Extrusão a Baixas Temperaturas.
Palabras clave en portugués
irradiação
latex de borracha natural
otimização
processo
Resumen en portugués
O látex de borracha natural foi formulado, radiovulcanizado e, em seguida, estabilizado radioliticamente (GAMATEX), para ser empregado na fabricação de artefatos de borracha utilizados na área médica. A eficiência de reticulação do látex, quando radiovulcanizado com raios gama, correlacionou-se matematicamente com a razão de concentração do sistema de radiosensibilizador (x1 = [An-B] / [KOH]) e com a dose de vulcanização (x2), apresentando alto grau de interação, segundo o seguinte modelo matemático: , onde representa a resistência à tração na ruptura. O processo RVNRL foi otimizado para baixas doses de vulcanização e altas concentrações de An-B. A resistência radioxidativa da borracha, obtida a partir do GAMATEX, foi atingida adicionando-se uma mistura de antioxidantes (45% BANOX S + 55% TNPP). Esta mistura apresentou um efeito sinérgico. O látex apresentou comportamento pseudoplástico com a ocorrência de tensão de escoamento. A taxa de desestabilização irreversível do látex foi diretamente proporcional à [An-B] e inversamente proporcional à [KOH]. O efeito pós-irradiação do látex ou a desestabilização reversível, ocorreu devido à presença de uma concentração residual de An-B que não reagiu. A irradiação melhorou a estabilidade coloidal do GAMATEX, devido ao aumento da tixotropia e da tendência newtoniana além da correlação entre o grau de consistência (k) e o índice pseudoplástico (n), de acordo com o modelo matemático . Este fato permite um tempo maior de estocagem do GAMATEX. A viscosidade relativa do látex correlaciona-se com a temperatura e com o teor da borracha seca conforme o modelo matemático: , onde rw é a razão (BS/100-BS). O látex radiovulcanizado coagulou à temperatura de –10ºC no sistema de refrigeração projetado.
Título en inglés
DEVELOPMENT OF MEDICAL TUBE FABRICATION PROCESS FROM RVNRL: OTIMIZATION AND EXTRUTION DEVICE AT LOW TEMPERATURE
Palabras clave en inglés
gamma radiation
natural rubber latex
otimization
process
Resumen en inglés
The natural rubber latex was formulated, irradiation vulcanized and stabilized (GAMATEX) to make rubber goods for medical purpose. When the latex was vulcanized by gamma rays the effectiveness crosslinking of GAMATEX relationship between the concentration ratio of sensitizer system (x1=[n-BA]/[KOH]) and the vulcanization dose (x2), showing high interaction grade according to the following the mathematical equation: , where is the tensile strength. The RVNRL process was optimized for low vulcanization doses and high concentrations of n-BA. The resistance to radiolitic oxidation of rubber obtained from GAMATEX was attained when one antioxidants mixture (45% BANOX S + 55% TNPP) was added. This mixture exhibited synergetic effect. The latex showed pseudoplastic rheological behavior and the yield stress occurrence. The irreversible destabilization rate of latex was direct proportional to [n-BA] and indirect proportional to [KOH]. The post-irradiation effects or reversible destabilization of latex occurred because there is a residual concentration of [n-BA] that it was not reacted. The colloidal stability of GAMATEX improved with irradiation, showing showing the increase of thixotropic behavior and the tendency to newtonian behavior flow besides the relationship between the viscosity index (k) and the pseudoplastic index (n) according to the mathematical model: . This fact allows the higher storage time of GAMATEX. The relative viscosity of latex was relationship between the temperature and the total dry rubber content according to the mathematical model: , where rw is the ratio (BS/100-BS). The radiation vulcanized latex coagulated at –10ºC into the projected freezing system.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2004-07-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.