Disertación de Maestría
DOI
10.11606/D.85.1998.tde-14022002-175024
Documento
Autor
Nombre completo
Daniel Zanetti de Florio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1998
Director
Tribunal
Muccillo, Reginaldo (Presidente)
Toffoli, Samuel Marcio
Varela, Jose Arana
Título en portugués
Estudos de Sinterização e de Envelhecimento Térmico de Cerâmicas de Zircônia - Ítria por Espectroscopia de Impedância
Palabras clave en portugués
espectroscopia de impedância
sinterização
zircônia
Resumen en portugués
Eletrólitos sólidos cerâmicos de ZrO2:8% mol Y2O3 foram preparados com pós de três origens: pó comercial fabricado pela Nissan (Japão), pó obtido por coprecipitação dos hidróxidos no IPEN e pó obtido por mistura de óxidos (utilizando-se ZrO2 produzido na Usina de Zircônio do IPEN e Y2O3 (USA) de pureza superior a 99,9%). Esses materiais de partida foram analisados pelas seguintes técnicas: fluorescência de raios X para a determinação dos teores de ítrio, difração de raios X para a determinação das fases, sedimentação para a determinação da distribuição do tamanho de partículas, adsorsão gasosa (BET) para a determinação da área de superfície específica e microscopia eletrônica de transmissão para a determinação do tamanho médio de partícula. Amostras compactadas foram analisadas por dilatometria para avaliar os estágios de sinterização. As amostras sinterizadas foram caracterizadas por difração de raios X para análise de fases e microscopia eletrônica de varredura para análise da morfologia dos grãos. Análises por espectroscopia de impedância foram feitas para acompanhar o envelhecimento térmico dos eletrólitos sólidos de zircônia-ítria a 600 ºC, temperatura de trabalho do sensor permanente de oxigênio, e para estudar a sua cinética de sinterização. Os principais resultados mostram que o envelhecimento térmico a 600 ºC diminui a resposta (fem) do sensor nas primeiras 100 h até um valor estável. Além disso, os estudos de sinterização por espectroscopia de impedância permitiram encontrar correlações entre parâmetros elétricos, a cinética de sinterização e os mecanismos de crescimento de grão.
Título en inglés
Sintering and Thermal Ageing Studies of Zirconia - Yttria Ceramics by Impedance Spectroscopy
Palabras clave en inglés
impedance spectroscopy
sintering
Resumen en inglés
ZrO2:8 mol %Y2O3 solid electrolyte ceramic pellets have been prepared with powders of three different origins: a Nissan (Japan) commercial powder, a powder obtained by the coprecipitation technique at IPEN, and the mixing of powder oxides (ZrO2 produced at a Pilot Plant at IPEN and 99.9% pure Y2O3 of USA origin). These starting powders have been analysed by the following techniques: X-ray fluorescence for yttrium content, X-ray diffraction for structural phase content, sedimentation for particle size distribution, gas adsorption (BET) for surface area determination, and transmission electron microscopy for average particle size determination. Pressed ceramic pellets have been analysed by dilatometry to evaluate the sintering stages. Sintered pellets have been characterized by X-ray diffraction for phase analysis and scanning electron microscopy for grain morphology analysis. Impedance spectroscopy analysis have been carried out to follow thermal ageing of zirconia-yttria solid electrolyte at 600 ºC, the working temperature of permanent oxygen sensor, and to study sintering kinetics. The main results show that ageing at 600 ºC decreases the emf sensor response in the first 100 h to a steady value. Moreover, sintering studies by impedance spectroscopy allowed for finding correlations between electrical parameters, sintering kinetics and grain growth mechanisms.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
M21658.pdf (2.06 Mbytes)
Fecha de Publicación
2004-02-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.