• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Luiza Ferreira Sobrinho
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2018
Directeur
Jury
Sakata, Solange Kazumi (Président)
Casini, Julio César Serafim
Polo, André Sarto
Titre en portugais
Oxidação eletroquímica do etanol em eletrólito alcalino utilizando nanocompósito a base de grafeno/paládio
Mots-clés en portugais
célula à combustível
óxido de grafeno
paládio
voltametria cíclica
Resumé en portugais
Nesse estudo foi sintetizado e caracterizado o óxido de grafeno (OG) a partir do método de Hummers modificado. O OG foi utilizado como suporte para nanopartículas de paládio para uso como eletrocatalisador em células a combustíveis abastecidas diretamente a etanol. O uso de carbono grafite como suporte de nanopartículas metálicas é deteriorado com mais rapidez, levando a diminuição do tempo de vida útil da célula a combustível. O objetivo principal foi a incorporação do paládio no óxido de grafeno via feixe de elétrons, e a comparação com o catalisador incorporado por via química, utilizando o borohidrato de sódio. Foram utilizadas técnicas de caracterização tais como: termogravimetria (TG), difração de raios-X (DRX), as espectroscopias de Raman e infravermelho com transformada de Fourier (FT-IR), microscopia de transmissão eletrônica (MET), Espectroscopia de fotoelétrons por raios- X (XPS) e estudos voltamétricos como a voltametria cíclica e cronoamperometria. Os resultados indicaram que para a dose de 288 kGy, houve a incorporação, porém, não foi suficiente para que houvesse a redução dos grupos oxigenados, estudos com o oxido de grafeno previamente reduzido via térmica e incorporado via feixe de elétrons foram comparados na mesma dose.
Titre en anglais
Electrochemical oxidation of ethanol in alkaline electrolyte using graphene / palladium base nanocomposite
Mots-clés en anglais
cyclic voltammetry
fuel cell
graphene oxide
palladium
Resumé en anglais
In this study, graphene oxide (GO) was synthesized by the modified Hummers method and characterized. GO was used as support for palladium nanoparticles as an electrocatalyst on direct ethanol fuel cell (DEFC). One of the drawbacks using carbon graphite as a support for metal nanoparticles was because it deteriorates more quickly, leading to shortened fuel cell life. The main objective was the incorporation of Pd on the graphene oxide by the electron beam and was compared with the chemical incorporation, using sodium borohydride. Characterization techniques such as thermogravimetry (TG), X-ray diffraction (XRD), Raman spectroscopy and Fourier transform infrared (FT-IR), electron transmission microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and voltammetric studies such as cyclic voltammetry and chronoamperometry. The results indicated that at a dose of 288 kGy, there was an incorporation, however, it was not enough for there to be a decrease in the groups of oxygenates, studies with the graphene oxide downloaded through the thermal and through electron beams were compared in the same dose.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-06-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.