Master's Dissertation
DOI
https://doi.org/10.11606/D.85.1986.tde-25062012-094540
Document
Author
Full name
Michelangelo Durazzo
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 1985
Supervisor
Committee
Ramanathan, Lalgudi Venkataraman (President)
Ambrozio Filho, Francisco
Wolynec, Stephan
Title in Portuguese
Corrosão de placas combustíveis tipo MTR contendo núcleos de cermets U3O8-Al
Keywords in Portuguese
cermets
corrosão
óxidos de urânio
Abstract in Portuguese
Foram fabricadas amostras de placas combustíveis contendo núcleos de cermets U3O8-Al com concentrações de U3O8 variando de 10 a 90% em peso (3,4 a 55,5% em volume). Amostras contendo núcleos com 58% em peso de U3O8, foram fabricadas a partir de compactados com densidades variando de 75 a 95% da densidade teórica. É discutida a influência da concentração de U3O8 e da porosidade do compactado de partida sobre a porosidade e uniformidade da espessura do núcleo obtido. Os núcleos U3O8-Al foram submetidos a ensaios de corrosão por água deionizada nas temperaturas 30, 50, 70 e 90°C, onde os núcleos foram expostos através de um defeito artificial produzido no revestimento. Os resultados obtidos mostram que a corrosão dos núcleos é acompanhada pela liberação de hidrogênio. O volume total de hidrogênio liberado (V) e o tempo transcorrido até que seja observado o início da liberação de hidrogênio (tempo de incubação ti, são dependentes da porosidade do núcleo e da temperatura absoluta (T), podendo ser descritos pelas equações: V = K1 eα1 P - K2 T eα2 P e ti = eK1 + K2 P + K3 / T + K4 P / T onde P é a fração volumétrica de vazios (porosidade) e K1, K2, K3,K4, α1 e α2 são constantes. É proposto e discutido um mecanismo para o processo de corrosão de núcleos U3O8-Al. O revestimento das amostras de placas combustíveis foi submetido a ensaios de corrosão sob condições similares às encontradas no reator IEA-R1 operando às potências de 2 MW, 5 MW e 10 MW. Foi verificado o efeito da presença de heterogeneidades superficiais e de um tratamento de limpeza química sobre o comportamento da corrosão do revestimento. Os resultados obtidos mostram que a corrosão é regulada pela dissolução/erosão da camada de óxido formada e segue lei linear para as três condições de testes e que a presença de heterogeneidades superficiais ou o tratamento de limpeza química não alteram significativamente a corrosão do revestimento para tempos de exposição de até 20 dias. Estão apresentadas as velocidades de corrosão e as espessuras das camadas de óxido observadas nos três ensaios efetuados. Não foi observado ataque localizado significativo.
Title in English
Corrosion of MTR type fuel plates containing U3O8-Al cermet cores
Keywords in English
cermets
corrosion
fuel plates
uranium oxides U3O8
Abstract in English
Fuel plate specimens containing U3O8-Al cermet cores were fabricated with the U3O8 concentration varying between 10 and 90% by weight (3.4 to 55.5% in volume). Fuel plate specimens containing 58% U3O8 by weight were also fabricated from compacts with densities varying between 75 and 95% of the theoretical density. The influence of U308 concentration and porosity of the initial compact on the porosity and uniformity of thickness of the core are discussed. The U3O8-Al cores were corrosion tested in deionized water at 30, 50, 70 and 90°C, where in the cores were exposed to the deionized water by means of an artificially produced cladding defect. The results indicate that core corrosion is accompanied by hydrogen evolution. The total volume of hydrogen evolued (V) and the time to initiation of hydrogen evolution (incubation time ti), vary with the porosity of the core and temperature (T), according to equations: V = K1 eα1 P - K2 T eα2 P e ti = eK1 + K2 P + K3 / T + K4 P / T where P is the volumetric fraction of pores and K1, K2, K3,K4, α1 e α2, are constants. A mechanism for the U3O8-Al core corrosion has been proposed and discussed. The cladding of the fuel plats specimens was also corrosion tested under conditions similar to those encountered in the IEA-R1 reactor operating at 2, 5 and 10 MW. The effect of the presence of surface heterogeneities and a chemical surface treatment on the corrosion behavior of the cladding have been studied. The results reveal that the corrosion is regulated by dissolution/erosion of the oxide layer, and follows a linear law under the three test conditions. The presence of surface heterogeneities or the chemical surface treatment did not significantly alter the cladding corrosion for test times of up to 20 days. The corrosion rates and the oxide layer thicknesses observed under the three test conditions are also presented. No significant localized attack was observed.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2012-07-23
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.