• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.85.2008.tde-02062009-163925
Documento
Autor
Nombre completo
Gilberto de Oliveira Moraes
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Lugão, Ademar Benévolo (Presidente)
Parra, Duclerc Fernandes
Wiebeck, Helio
Título en portugués
Obtenção de membranas trocadoras de prótons a base de polietileno para uso em células à combustível
Palabras clave en portugués
exertia
membranas
polietileno
Resumen en portugués
A enxertia induzida por radiação do polietileno (PE) e estireno (ST), via fonte de 60 Co foi conduzida usando irradiação direta (simultânea) e indireta (pré- irradiação e peroxidação) á temperatura ambiente. As doses irradiadas, em ambos os caso, foi de 0,5 kGy até 80 kGy. Pelo método da irradiação simultânea, os filmes foram imersos em mistura estireno: metanol (30:70 v/v) mais 30% de aditivo (ácido sulfúrico) em ampolas de vidro de 40 mL sob atmosfera inerte, seladas em atmosfera inerte, para então, serem irradiadas em instalações industriais (EMBRARAD / CBE). Após a irradiação, as amostras foram retiradas, lavadas e secas em estufas, por 8 horas e pesadas para cálculo de grau de enxertia. Pelo método da pré-irradiação, as amostras foram irradiadas em ampolas, seladas sob atmosfera inerte. A mistura acima mencionada era adicionada após a irradiação, A enxertia propriamente se inicia no momento de adição de mistura. Após 8 horas, as amostras eram retiradas, secas e pesadas para cálculo de grau de enxertia. No método da peroxidação, as amostras foram seladas com ar (oxigênio). Todo o procedimento do método pré-irradiação era então repetido. As amostras que apresentaram grau de enxertia (DOG na sigla em inglês) significativo eram caracterizadas (TGA, DSC) e sulfonadas para cálculo de capacidade de troca iônica (IEC na sigla em inglês). Observou-se que, pelo método indireto, as amostras não apresentaram enxertia significativa. Pelo método direto (simultânea) as amostras apresentaram modificação (aumento de massa), ou seja, houve enxertia, mas não apresentaram IEC significativo. A dose que apresentou o melhor DOG foi 80 kGy.
Título en inglés
POLYETHYLENE (PE) BASED PROTON EXCHANGE MEMBRANE FOR USE IN FUEL CELL
Palabras clave en inglés
enxertia
membranas
polietileno
Resumen en inglés
The irradiation – induced graft of styrene onto polyethylene (PE) in a Cobalt-60 source was carried out using direct (simultaneous) and indirect (preirradiation and peroxidation) methods at room temperature. The dose applied in both cases varied from 0,5 to 80 kGy; In the direct method, the films were immersed in a solution of styrene: methanol (30:70 v/v) and 30% of sulfuric acid(additive) in glass ampoules of 40 mL under inert atmosphere, and then irradiated. After irradiation process, the samples were kept in solution for 8 hours and taken off the ampoules, dried in oven at 60 0C for another 8 hour period until constant weight. In pre-irradiation method, the samples were irradiated in dry and sealed ampoules, under inert atmosphere. The solution was then added to the samples, and after 8 hours, taken off, dried, sealed and weighted. In peroxidation method, the difference was not inert atmosphere but atmosphere of air (O2).For each samples it was calculated the degree of grafting (DOG). The samples that showed some DOG were sulfonated, characterized (DSC, TGA and infrared) and the ion exchange capacity (IEC) was calculated. The samples processed by indirect method presented no DOG at all. The samples processed by direct method present grafting (best result was 80 kGy). These samples, after sulfonated, presented ion exchange properties.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.