Master's Dissertation
DOI
10.11606/D.85.2016.tde-04042016-140231
Document
Author
Full name
Mariana Silva de Araujo
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2016
Supervisor
Committee
Genova, Luís Antonio (President)
Castanho, Sonia Regina Homem de Mello
Ferreira, Eduardo Bellini
Title in Portuguese
Utilização de resíduos de catalisador (ECAT) e cinzas da casca de arroz (CCA) na elaboração de vidros silicatos soda-cal destinados a embalagem
Keywords in Portuguese
cinza da casca de arroz
resíduos de catalisador exaurido
resíduos sólidos industriais
vidros
vidros soda-cal
Abstract in Portuguese
Estudo realizado acerca da utilização de dois resíduos sólidos industriais (RSI) gerados em grande quantidade no Brasil, na obtenção de vidros soda-cal destinados à produção de embalagens. Os resíduos avaliados foram a cinza de casca de arroz (CCA) e resíduo do catalisador usado das unidades de Craqueamento Catalítico Fluido das Petroquímicas (ECAT), ambos podem ser classificados como resíduos sólidos de classe II de acordo com a norma NBR 10.004. Esta nova proposta para destinação desses resíduos é uma alternativa às atuais disposições, buscando não apenas minimizar os impactos ambientais gerados, mas também a valorização dos mesmos como matérias-primas. Para a produção das amostras, além da utilização dos RSIs, foram também utilizados óxidos fundente (Na2CO3) e estabilizante (CaO). Os resultados obtidos demonstraram que ambos podem ser usados como recebidos (sem tratamento prévio) substituindo matérias-primas importantes, fontes de Al2O3 e SiO2, necessárias para a formação de vidros. As amostras obtidas apresentaram a cor âmbar devido a presença de níquel (íons Ni2+) proveniente do ECAT e transmitância óptica de 18%. Estas, ainda demonstraram boa homogeneidade, i.e., ausência de bolhas e estriais e, resistências hidrolíticas média de 1,33x10-8 g/cm²·dia (superior à um vidro comercial de composição semelhante) de acordo com a ISO695-1984. O vidro obtido é adequado para aplicações que exigem baixa transmitância como embalagens de vidros em geral, os quais não requerem perfeita visibilidade e transparência. O teor de incorporação na composição final das amostras foi de aproximadamente 78% em massa.
Title in English
Use of rice rusk ash and spent catalyst as a source of raw material for the production and characterization of soda-lime silicate glasses destined for packaging
Keywords in English
glass
industrial solid waste
rice husk ash
soda-lime glass
spent catalyst
Abstract in English
In this study, the use of two industrial solid wastes (ISW), generated in large quantities in Brazil, were presented in production of soda-lime silicate glasses destined for packaging. The evaluated wastes were rice husk ash (RHA) and the spent catalyst at the Petrochemical Fluid Catalytic Cracking units (ECAT), both may be classified as a class II solid waste according to NBR 10.004. This new proposal for the allocation of such wastes is an alternative to current provisions, seeking not only to minimize environmental impacts, but also enrich them as raw materials. For the samples production, besides ISW were used melting oxide (Na2CO3) and stabilizer oxide (CaO).The results demonstrate that both can be used in their raw form (without treatment) replacing important raw materials, sources of Al2O3 and SiO2, essential for glass formation. The samples obtained presented amber color due to the presence of nickel (Ni²+ ion) from ECAT and 18% of optical transmittance. They also showed a good homogeneity, i.e., absence of bubbles and striae and 1,33x10-8 g/cm²·day of hydrolytic resistance according to ISO695-1984. Thus, the obtained glass is suitable for applications requiring low light transmittance such as colored glasses containers in general, which does not require perfect visibility and transparency. The incorporation in the final composition was approximately 78% in mass.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-04-07
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.