Disertación de Maestría
DOI
10.11606/D.85.2013.tde-04072013-132158
Documento
Autor
Nombre completo
Rodolfo Molina Antoniassi
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Spinacé, Estevam Vitorio (Presidente)
Batista, Elisete Aparecida
Farias, Luciana Aparecida
Título en portugués
Desempenho elétrico e distribuição dos produtos da célula a combustível com etanol direto utilizando Pt/C, PtSn/C(liga) e PtSnO2/C como eletrocatalisadores anódicos
Palabras clave en portugués
célula a combustível a etanol direto
eletro-oxidação do etanol
eletrocatalisadores
PtSn/C
Resumen en portugués
No presente trabalho, o desempenho elétrico dos eletrocatalisadores anódicos Pt/C, Pt3Sn/C(liga), Pt(SnO2)/C, Pt3(SnO2)/C e Pt9(SnO2)/C para as reações de eletro-oxidação de etanol, acetaldeído e ácido acético foi investigado. Testes em célula unitária mostraram que a adição de Sn seja na forma de liga Pt-Sn ou na forma de óxido (SnO2) coexistente com a platina metálica aumenta consideravelmente a resposta elétrica gerada pela célula. A melhora no desempenho elétrico dos catalisadores a base de PtSn é resultado da capacidade em oxidar o acetaldeído, majoritariamente produzido pelo Pt/C, em ácido acético. Pt3(SnO2)/C exibiu a melhor resposta elétrica tanto para o etanol quanto para acetaldeído como combustíveis, alcançando valores de densidade de potência máxima de 127 e 58 mW cm-2, respectivamente. Misturas entre os combustíveis mostraram que o acetaldeído é um composto que leva a uma rápida desativação dos catalisadores, enquanto que o ácido acético, embora não seja oxidado a CO2 nas condições de operação, não afeta o desempenho elétrico da célula.
Título en inglés
Electrical performance and products distribution of direct ethanol fuel cell using Pt/C, PtSn/C(alloy) and PtSnO2/C as anodic electrocatalysts
Palabras clave en inglés
direct ethanol fuel cell
electrocatalysts
ethanol electro-oxidation
PtSn/C
Resumen en inglés
In the present work, the electrical performance of the anodic electrocatalysts Pt/C, Pt3Sn/C(alloy), Pt(SnO2)/C, Pt3(SnO2)/C and Pt9(SnO2)/C towards ethanol, acetaldehyde and acetic acid electro-oxidation reactions was investigated. Single cell tests showed that the Sn addiction whether in Pt-Sn alloyed form or in oxide (SnO2) form coexisting with metallic platinum increases considerably the electrical response generated by the cell. The electrical performance improvement of PtSn-basis catalysts is a result of the ability to oxidize acetaldehyde, mostly produced by Pt/C, in acetic acid. Pt3(SnO2)/C exhibited the highest electrical performance both for ethanol and acetaldehyde as fuels, reaching maximum power density values of 127 and 58 mW cm-2, respectively. Mixtures between fuels showed that acetaldehyde is a compound which leads a rapid deactivation of the catalysts, while acetic acid, although not oxidized to CO2 under operating conditions, does not affect the cell electrical performance.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-07-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.