Doctoral Thesis
DOI
10.11606/T.85.2014.tde-04122014-143143
Document
Author
Full name
Rafael Morgado Batista
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2014
Supervisor
Committee
Muccillo, Eliana Navarro dos Santos (President)
Escote, Marcia Tsuyama
Fonseca, Fabio Coral
Genova, Luís Antonio
Toffoli, Samuel Marcio
Title in Portuguese
Efeitos da atmosfera de sinterização e do tamanho de partícula na sinterização da céria-gadolínia
Keywords in Portuguese
céria-gadolínia
curva mestre de sinterização
sinterização
Abstract in Portuguese
Os efeitos da atmosfera de sinterização e do tamanho inicial das partículas na sinterização da céria contendo 10% em mol de gadolínia (GdO1,5) foram sistematicamente estudados neste trabalho. Materiais de partida com três valores para a área de superfície específica foram utilizados, 210 m2/g, 36,2 m2/g e 7,4 m2/g. Diferentes cinéticas de sinterização foram verificadas. Quanto menor o tamanho inicial das partículas, menor é a temperatura para o início da sinterização e mais acelerada a densificação do material. Curvas mestres de sinterização foram construídas para cada um dos materiais analisados. Um programa computacional foi especialmente desenvolvido para este propósito. Diferenças significativas entre as energias de ativação para densificação foram verificadas. Para este trabalho foi determinado que, quanto menor o tamanho inicial de partícula, menores as energias de ativação. A evolução das distribuições de tamanhos de cristalitos foi investigada para os materiais de maior área superficial específica. Foi determinado que a eliminação e migração de poros (pore drag) é o mecanismo predominante para o crescimento de grãos durante o início da sinterização da céria gadolínia. Os efeitos da atmosfera de sinterização no desvio de estequiometria, na densificação, na evolução microestrutural e na condutividade elétrica da céria-gadolínia foram analisados. Atmosferas redutoras, oxidantes e inertes foram usadas para este propósito. Desvios na estequiometria da céria foram verificados no volume do material, sendo este dependente da área de superfície específica e da atmosfera utilizada. Quanto maior o potencial de redução da atmosfera utilizada, maior a concentração de Ce3+ no material. Com o aumento da concentração de Ce3+ um aumento no tamanho médio de grãos foi verificado. Uma diminuição na condutividade elétrica total, intra e intergranular foram determinadas para as amostras sinterizadas em atmosferas redutoras.
Title in English
Effects of sintering atmosphere and the particle size on sintering of gadolinia-doped ceria
Keywords in English
gadolinia-doped ceria
master sintering curve
sintering
Abstract in English
The effects of the sintering atmosphere and initial particle size on the sintering of ceria containing 10 mol% gadolinia (GdO1.5) were systematically investigated. The main physical parameter was the specific surface area of the initial powders. Nanometric powders with three different specific surface areas were utilized, 210 m2/g, 36,2 m2/g e 7,4 m2/g. The influence on the densification, and micro structural evolution were evaluated. The starting sintering temperature was verified to decrease with increasing on the specific surface area of raw powders. The densification was accelerated for the materials with smaller particle size. Sintering paths for crystallite growth were obtained. Master sintering curves for gadolinium-doped ceria were constructed for all initial powders. A computational program was developed for this purpose. The results for apparent activation energy showed noticeable dependence with specific surface area. In this work, the apparent activation energy for densification increased with the initial particle size of powders. The evolution of the particle size distributions on non isothermal sintering was investigated by WPPM method. It was verified that the grain growth controlling mechanism on gadoliniadoped ceria is the pore drag for initial stage and beginning of intermediate stage. The effects of the sintering atmosphere on the stoichiometry deviation of ceria, densification, microstructure evolution, and electrical conductivity were analyzed. Inert, oxidizing, and reducing atmospheres were utilized on this work. Deviations on ceria stoichiometry were verified on the bulk materials. The deviation verified was dependent of the specific surface area and sintering atmosphere. Higher reduction potential atmospheres increase Ce3+ bulk concentration after sintering. Accelerated grain growth and lower electrical conductivities were verified when reduction reactions are significantly present on sintering.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2014-12-22
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.