Disertación de Maestría
DOI
10.11606/D.85.2011.tde-07112012-073635
Documento
Autor
Nombre completo
Henrique Perez Ferreira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Lugão, Ademar Benévolo (Presidente)
Brant, Antonio Jedson Caldeira
Torresi, Susana Ines Cordoba de
Título en portugués
Modificação de poli(fluoreto de vinilideno) induzida por radiação gama para aplicação como compósito ionomérico de metal-polímero
Palabras clave en portugués
compósito ionomérico de metal-polímero
enxertia
estireno
induzida por radiação
poli (fluoreto de vinilideno)
PVDF
Resumen en portugués
Foi estudada a enxertia de estireno induzida por radiação gama em filmes de poli(fluoreto de vinilideno) (PVDF) com espessura de 0,125 mm com doses entre 1 e 100 kGy em presença de soluções de estireno/N,Ndimetilformamida (DMF) (1:1, v/v) e estireno/tolueno (1:1, v/v) com taxa de dose de 5 kGy.h-1 por meio do método simultâneo de irradiação sob atmosfera de nitrogênio e em temperatura ambiente, usando raios gama de uma fonte de Co- 60. Depois de enxertados, os polímeros foram sulfonados em soluções de ácido clorossulfônico/1,2-dicloroetano (2 e 10 %). Os filmes foram caracterizados antes e depois de cada modificação com o cálculo do Grau de enxertia, (DOG), espectrometria no infravermelho (FT-IR), microscopia eletrônica de varredura (MEV), calorimetria exploratória diferencial (DSC) e termogravimetria (TG/DTG). Os resultados do grau de enxertia mostraram que a enxertia aumenta com o aumento da dose e varia enormemente de acordo com o solvente utilizado, com enxertias cerca de 20 vezes maiores quando do uso da DMF em relação ao do tolueno. Foi possível confirmar a enxertia do estireno por FT-IR graças ao aparecimento de novos picos característicos e por TG/DTG e DSC por meio das alterações do comportamento térmico dos materiais enxertados/sulfonados. Os materiais sulfonados ainda foram caracterizados por suas capacidades de troca iônica (IEC), que mostraram que tanto os aumentos do grau de enxertia quanto os da concentração do ácido clorossulfônico aumentam o IEC. Os resultados mostraram que é possível obter materiais com capacidades de troca iônica com possibilidade de aplicação como compósitos ionoméricos de metal-polímero.
Título en inglés
Poly(vinylidene fluoride) modification induced by gamma irradiation for application as ionic polymer-metal composite
Palabras clave en inglés
grafting
ionic polymer-metal composite
poly(vinylidene fluoride)
PVDF
radiation induced
styrene
Resumen en inglés
Gamma-radiation-induced grafting of styrene into poly(vinylidene fluoride) (PVDF) films with 0.125 mm thickness at doses from 1 to 100 kGy in the presence of a styrene/N,N- dimethylformamide (DMF) solution (1:1, v/v) and styrene/toluene (1:1, v/v) at dose rate of 5 kGy h-1 was carried out by simultaneous method under nitrogen atmosphere at room temperature, using gamma rays from a Co-60. After grafting reactions, the polymer was then sulfonated in chlorosulfonic acid/1,2-dichloroethane (2 and 10%) for 3 hours. The films were characterized before and after modification by calculating the degree of grafting (DOG), infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and thermogravimetry (TG/DTG). DOG results show that grafting increases with dose, and varies enormously depending on the solvent used, with DOGs about 20 times greater in DMF than in toluene. It was possible to confirm the grafting of styrene by FT-IR due to the appearance of the new characteristic peaks and by the TG and DSC which exhibited changes in the thermal behavior of the grafted/sulfonated material. Sulfonated material was also characterized by ion exchange capacity (IEC) showed that both DOG and sulfonic acid concentration increase IEC values. Results showed that it is possible to obtain materials with ion exchange capacity of possible application as ionic polymer-metal composites.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-11-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.