Tesis Doctoral
DOI
10.11606/T.85.2013.tde-09012014-144413
Documento
Autor
Nombre completo
Rafael Nogueira Bonifacio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Linardi, Marcelo (Presidente)
Farias, Luciana Aparecida
Forbicini, Christina Aparecida Leão Guedes de Oliveira
Poço, João Guilherme Rocha
Spinacé, Estevam Vitorio
Título en portugués
Estudo e desenvolvimento de conjuntos membrana-eletrodos (MEA) para célula a combustível de eletrólito polimérico condutor de prótons (PEMFC) com eletrocatalisadores à base de paládio
Palabras clave en portugués
célula a combustível de eletrólito polimérico condutor de prótons (PEMFC)
conjunto membrana-eletrodos (MEA)
eletrocatalisador
estimativa de custo de MEAs
paládio
Resumen en portugués
Sistemas de PEMFC são capazes de gerar energia elétrica com alta eficiência e baixa ou nenhuma emissão de poluentes, porém questões de custo e durabilidade impedem sua ampla comercialização. Nesse trabalho foi desenvolvido um MEA com eletrocatalisadores à base de paládio. Foram sintetizados e caracterizados eletrocatalisadores Pd/C, Pt/C e Ligas PdPt/C com diferentes razões entre metais e carbono. Foi realizado um estudo da razão entre ionômero de Nafion e eletrocatalisador para formação de triplas fases reacionais de máximos desempenhos, criado um modelo matemático para transpor esse ajuste para eletrocatalisadores com diferentes razões entre metal e suporte, considerando os aspectos volumétricos da camada catalisadora, e então realizado um estudo da espessura da camada catalisadora. Para as caracterizações foram utilizadas as técnicas de Difração de Raios-X, Microscopias Eletrônicas de Transmissão e de Varredura, Energia Dispersiva de Raios-X, Picnometria a Gás, Porosimetria por Intrusão de Mercúrio, Adsorção de Gás, segundo as equações de BET e BJH, Análise Termo Gravimétrica e feitas as determinações de diâmetros de partículas, de áreas de superfície específica e de parâmetros de rede. Todos os eletrocatalisadores foram usados no preparo de MEAs que foram avaliados em célula unitária de 5 cm2 entre 25 e 100 °C a 1 atm; e a melhor composição foi avaliada também a 3 atm. No estudo dos metais para as reações, visando reduzir a platina aplicada aos eletrodos, sem perdas de desempenho, foram selecionados Pd/C para ânodos e PdPt/C 1:1 para cátodos. A estrutura de MEA desenvolvida utilizou 0,25 mgPt.cm-2 e resultou em densidades de potência de até 550 mW.cm-2 e potências de até 2,2 kWe por grama de platina. A estimativa realizada mostrou que houve uma redução de até 64,5 % nos custos em relação à estrutura de MEA previamente conhecida. Em função da temperatura e pressão de operação foram obtidos valores a partir de R$ 3.540,73 para o preparo de MEAs para cada quilowatt instalado. Com base em estudos recentes, concluiu-se que o custo do MEA desenvolvido é compatível às aplicações estacionárias de PEMFC.
Título en inglés
Study and development of membrane electrode assemblies for proton exchange membrane fuel cell (PEMFC) with palladium based catalysts
Palabras clave en inglés
catalyst
MEAs cost estimation
membrane electrode assemblie (MEAs)
palladium
proton exchange membrane fuel cell (PEMFC)
Resumen en inglés
PEMFC systems are capable of generating electricity with high efficiency and low or no emissions, but durability and cost issues prevent its large commercialization. In this work MEA with palladium based catalysts were developed, Pd/C, Pt/C and alloys PdPt/C catalysts with different ratios between metals and carbon were synthesized and characterized. A study of the ratio between catalyst and Nafion Ionomer for formation of high performance triple-phase reaction was carried out, a mathematical model to implement this adjustment to catalysts with different relations between metal and support taking into account the volumetric aspects of the catalyst layer was developed and then a study of the catalyst layer thickness was performed. X-ray diffraction, Transmission and Scanning Electron Microscopy, X-ray Energy Dispersive, Gas Pycnometry, Mercury Intrusion Porosimetry, Gas adsorption according to the BET and BJH equations, and Thermo Gravimetric Analysis techniques were used for characterization and particle size, specific surface areas and lattice parameters determinations were also carried out. All catalysts were used on MEAs preparation and evaluated in 5 cm2 single cell from 25 to 100 °C at 1 atm and the best composition was also evaluated at 3 atm. In the study of metals for reactions, to reduce the platinum applied to the electrodes without performance losses, Pd/C and PdPt/C 1:1 were selected for anodes and cathodes, respectively. The developed MEA structure used 0,25 mgPt.cm-2, showing power densities up to 550 mW.cm-2 and power of 2.2 kWnet per gram of platinum. The estimated costs showed that there was a reduction of up to 64.5 %, compared to the MEA structures previously known. Depending on the temperature and operating pressure, values from US$ 1,475.30 to prepare MEAs for each installed kilowatt were obtained. Taking into account recent studies, it was concluded that the cost of the developed MEA is compatible with PEMFC stationary application.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-01-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.