Disertación de Maestría
DOI
10.11606/D.85.2009.tde-13102009-154057
Documento
Autor
Nombre completo
Glauson Aparecido Ferreira Machado
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Bressiani, Ana Helena de Almeida (Presidente)
Rocha, Rosa Maria da
Ussui, Valter
Título en portugués
Desenvolvimento de compósito cerâmico a partir de mistura de alumina e polímero pecursor  cerâmico polissilsesquioxano
Palabras clave en portugués
alumina
Compósito
pirólise
polissilsesquioxano
Resumen en portugués
O processamento de materiais cerâmicos, a partir de pirólise de polímeros precursores, tem sido intensivamente pesquisado no decorrer das últimas décadas, devido às vantagens que esta via proporciona, como: temperaturas de processo inferiores as das técnicas convencionais; controle da estrutura em nível molecular; possibilidade de síntese de grande variedade de compostos cerâmicos; obtenção de peças semi-acabadas; etc. O processo de pirólise controlada de polímero e carga ativa (AFCOP-active filler controlled polymer pyrolysis) possibilita a síntese de compósitos cerâmicos, por meio de reação entre cargas adicionadas (óxidos, metais, intermetálicos, etc.) e produtos sólidos e gasosos, provenientes da decomposição polimérica. Com base neste processo, no presente trabalho foram confeccionadas amostras de alumina, contendo adições de 10 e 20% em massa, de polímero precursor polissilsesquioxano. Estas foram pirolisadas a 900°C e tratadas termicamente em temperaturas de 1100, 1300 e 1500ºC, empregando-se taxa de aquecimento de 5°C/ min. e atmosfera de N2. As amostras foram caracterizadas em relação à densidade aparente, porosidade e dureza, após cada etapa de tratamento térmico. As transformações estruturais foram analisadas por difração de raios X, microscopia eletrônica de varredura e espectroscopia de infravermelho. As amostras tratadas até 1300°C resultaram em compósitos de alumina e oxicarbeto de silício, enquanto as tratadas a 1500°C, formaram compósitos de mulita e alumina. Na amostra da composição com 20% de polímero, se observou início de densificação em torno de 800°C e alta taxa de retração foi obtida a 1400°C.
Título en inglés
DEVELOPMENT OF CERAMIC COMPOSITES FROM MIXTURE OF ALUMINA AND CERAMIC PRECURSOR POLYMER POLY (SILSESQUIOXANE)
Palabras clave en inglés
alumina
Compósito
pirólise
polissilsesquioxano
Resumen en inglés
Processing of ceramics materials, by polymer precursors pyrolysis, has been intensively researched over the past decades, due to advantages that this path provides, such as: lower temperature process compared to conventional techniques; structure control at molecular level; synthesis possibility of a wide range of ceramic compounds; obtaining parts with dimensions of the final product etc. The active filler controlled polymer pyrolysis (AFCOP) process, enables the synthesis of ceramic composites, by reaction between added filler (oxides, metals, intermetallic etc.) and solid and gaseous products, from polymer decomposition. In this study, based on this process, samples of alumina, with addition of 10 and 20 mass% of poly silsesquioxane polymer precursor, were manufactured. These samples were pyrolyzed at 900 °C and thermal treated at temperatures of 1100, 1300 and 1500 °C. The samples were characterized for bulk density, porosity and hardness, after each stage of thermal treatment. Structural transformations were analyzed by X-ray diffraction, scanning electron microscopy and infrared spectroscopy. Samples treated until 1300 °C resulted in composites of alumina and silicon oxicarbide, while those treated at 1500 °C, formed composites of mullite and alumina. The samples with 20% of polymer added started to densify around 800°C and high retraction rate was observed at 1400°C.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-11-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.